Fabrication procedures for highly magnetically responsive lanthanide ion chelating polymolecular assemblies are presented. The magnetic response is dictated by the assembly size, which is tailored by extrusion through nanopore membranes. The assemblies' magnetic alignability and temperature-induced structural changes are monitored by birefringence measurements, a complimentary technique to nuclear magnetic resonance and small angle neutron scattering.
Bicelles are tunable disk-like polymolecular assemblies formed from a large variety of lipid mixtures. Applications range from membrane protein structural studies by nuclear magnetic resonance (NMR) to nanotechnological developments including the formation of optically active and magnetically switchable gels. Such technologies require high control of the assembly size, magnetic response and thermal resistance. Mixtures of 1,2-dimyristoyl-sn-glycero-3-phosphocholine (DMPC) and its lanthanide ion (Ln3+) chelating phospholipid conjugate, 1,2-dimyristoyl-sn-glycero-3-phospho-ethanolamine-diethylene triaminepentaacetate (DMPE-DTPA), assemble into highly magnetically responsive assemblies such as DMPC/DMPE-DTPA/Ln3+ (molar ratio 4:1:1) bicelles. Introduction of cholesterol (Chol-OH) and steroid derivatives in the bilayer results in another set of assemblies offering unique physico-chemical properties. For a given lipid composition, the magnetic alignability is proportional to the bicelle size. The complexation of Ln3+ results in unprecedented magnetic responses in terms of both magnitude and alignment direction. The thermo-reversible collapse of the disk-like structures into vesicles upon heating allows tailoring of the assemblies' dimensions by extrusion through membrane filters with defined pore sizes. The magnetically alignable bicelles are regenerated by cooling to 5 °C, resulting in assembly dimensions defined by the vesicle precursors. Herein, this fabrication procedure is explained and the magnetic alignability of the assemblies is quantified by birefringence measurements under a 5.5 T magnetic field. The birefringence signal, originating from the phospholipid bilayer, further enables monitoring of polymolecular changes occurring in the bilayer. This simple technique is complementary to NMR experiments that are commonly employed to characterize bicelles.
Bicelles are disk-like polymolecular assemblies obtained from numerous lipid mixtures.1,2,3,4,5 They are widely used for the structural characterization of membrane biomolecules by NMR spectroscopy.6,7 However, recent efforts aim to expand the field of possible applications.5,8,9 The most studied bicelle system is composed of a mixture of 1,2-dimyristoyl-sn-glycero-3-phosphocholine (DMPC), constituting the planar part of the assembly, and 1,2-dihexanoyl-sn-glycero-3-phosphocholine (DHPC) phospholipid covering the edge.1,2,3 The molecular geometry of the phospholipids composing the bilayer dictate the architecture of the self-assembled polymolecular structure.4,5 Replacing DHPC with DMPE-DTPA generates highly magnetically responsive and tunable bicelle systems.10,11 DMPC/DMPE-DTPA/Ln3+ (molar ratio 4:1:1) bicelles associate with many more paramagnetic lanthanide ions (Ln3+) on the bilayer's surface, resulting in an enhanced magnetic response.10 Moreover, replacing the water-soluble DHPC molecules with DMPE-DTPA/Ln3+ enables the formation of dilution-resistant bicelles.11
The magnetic alignability of planar polymolecular assemblies is dictated by their overall magnetic energy,
(1)
where B is the magnetic field strength, the magnetic constant, n the aggregation number and
the molecular diamagnetic susceptibility anisotropy of the lipids composing the bilayer. Therefore, the response of DMPC/DMPE-DTPA/Ln3+ bicelles to magnetic fields is tailored by their size (aggregate number n) and the molecular diamagnetic susceptibility anisotropy Δχ. The latter is readily achieved by changing the nature of the chelated Ln3+.12,13,14,15 Introducing cholesterol (Chol-OH) or other steroid derivatives in the bilayer offers the possibility of tuning both the aggregate number n and the magnetic susceptibility Δχ of the assemblies.11,16,17,18,19 For a given lipid composition, larger assemblies contain more lipids capable of contributing to the Emag (larger aggregate number n), resulting in more alignable species. The size of DMPC/DHPC bicelles, for example, is conventionally controlled through optimization of the composing lipid ratio or total concentration.20,21,22 Although this is possible in DMPC/DMPE-DTPA/Ln3+ bicelles, their thermo-reversible transformation from bicelle to vesicles upon heating offers added tailoring options. Mechanical means such as extrusion through membrane filters allows shaping of the vesicles. The magnetically alignable bicelles are regenerated upon cooling to 5 °C and their dimensions are dictated from the vesicle precursors.11 Herein, we focus on the potential of mechanical fabrication procedures with DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) or DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) as reference systems. The process works analogously when working with other Ln3+ than Tm3+. The wide range of possibilities offered by these techniques are highlighted in Figure 1 and extensively discussed elsewhere.23
Figure 1: Schematic overview of the possible fabrication procedures. The studied magnetically alignable Ln3+ chelating polymolecular assemblies are composed of either DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) or DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5). The dry lipid film is hydrated with a 50 mM phosphate buffer at a pH value of 7.4 and the total lipid concentration is 15 mM. An effective hydration of the lipid film requires either freeze thawing cycles (FT) or heating and cooling cycles (H&C). H&C cycles are necessary to regenerate samples after the last freeze thawing step, or to regenerate samples kept frozen over a prolonged period of time if they are to be used without further extrusion. These steps are extensively discussed by Isabettini et al.23 Maximally alignable polymolecular assemblies are achieved, delivering different assembly architectures based on the lipid composition. The bicelle size and magnetic alignability is tunable by extrusion (Ext) through nanopore membrane filters. The presented alignment factors Af were computed from 2D small angle neutron scattering (SANS) patterns of a DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) sample extruded through either 800, 400, 200, or 100 nm pores. SANS measurements are a complementary means of quantifying bicelle alignment that will not be covered in more detail herein.11,16 The Af ranges from -1 (parallel neutron scattering or perpendicular alignment of the bicelles with respect to the magnetic field direction) to 0 for isotropic scattering. Please click here to view a larger version of this figure.
The structure of bicelles has been extensively studied by a wide range of characterization techniques.13 The alignment of bicelles exposed to a magnetic field has been quantified by using either NMR spectroscopy or small angle neutron scattering (SANS) experiments.5,10,11,12,13,16,17,18,19,24,25 However, the shift and broadening of the NMR peaks occurring in the presence of Ln3+ are serious limitations to the method.15,26,27,28 Although SANS experiments do not suffer from this limitation, alternative and more accessible techniques are desirable for routine quantification of magnetically induced alignment of assemblies in solution. Birefringence measurements are a viable and comparatively simple alternative. Analogously to NMR experiments, birefringence measurements reveal valuable information on lipid rearrangements and lipid phases occurring in the bilayer. Moreover, geometric transformations occurring in the polymolecular assembly with changing environmental conditions such as temperature are monitored.11,12,13,16 Magnetically induced birefringence Δn′ has been used to study various types of phospholipid systems.13,29,30 Birefringence measurements based on the phase modulation technique in a magnetic field is a viable method to detect orientation of bicelles.12,16,18,29,31,32 The possibility of investigating bicelles with birefringence in high magnetic fields up to 35 T was also demonstrated by M. Liebi et al.13
When polarized light enters an anisotropic material, it will be refracted in an ordinary and extraordinary wave.11 The two waves have different velocities and are shifted in phase by a retardation δ. The degree of retardation δ is measured and converted into a birefringence signal to quantify the degree of anisotropy in the material using
(2)
where λ is the wavelength of the laser and d is the thickness of the sample. Phospholipids are optically anisotropic and their optical axis coincides with their long molecular axes, parallel to the hydrocarbon tails.11,12 No retardation is measured if the phospholipids are randomly orientated in solution. Retardation is measured when phospholipids are aligned parallel to each other. The magnetically induced birefringence can have a positive or negative sign depending on the orientation of the molecules in the magnetic field; see Figure 2. Phospholipids aligned parallel to the x-axis will result in a negative
, while those aligned along the z-axis result in a positive
. No birefringence is observed when the optical axis coincides with the direction of light propagation as the phospholipid aligns parallel to the y-axis.
Figure 2: Alignment of the phospholipids and corresponding sign of the magnetically induced birefringence . The sign of the measured
depends on the orientation of the phospholipid in the magnetic field. Dashed lines indicate the optical axis of the molecule. The light is polarized at 45° and propagates in the y direction. The magnetic field B is in the z direction. This figure has been modified from M. Liebi.11 Please click here to view a larger version of this figure.
In the case of an isotropic colloidal suspension of bicelles, the orientation induced by the arrangement of the phospholipids in the bilayer will be lost, zeroing the retardation δ. The bicelles must also align in order to orientate the optically active phospholipids in their bilayers, causing a retardation δ of the polarized light. Consequently, birefringence is a sensitive tool to quantify the magnetic alignability of polymolecular assemblies. Bicelles aligned perpendicular to the magnetic field will yield a positive , while those aligned parallel will yield a negative
. The sign depends on the alignment of the setup and may be checked with a reference sample.
1. Fabrication procedure for DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) and DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) polymolecular assemblies
Figure 3: Laboratory extruder used for bicelle and vesicle preparations. The extruder is assembled from the bottom up: (1) mount, (2) sample collecting space with a 2.4 mm (inner diameter) plastic outlet tube and o-ring, (3) and (4) large and small stabilizing mesh, (5) filter paper, (6) membrane filters, (7) o-ring, (8) jacketed vessel, (9) top cover with inlet and pressure connection, (10) cover, (11) butterfly screws, (12) pressure valve. A sketch of the assembled extruder is shown of the right-hand-side. The nitrogen gas (N2) is supplied by a pressure vessel and the jacketed vessel (9) is connected to a water bath for temperature control. The sample undergoes 10 extrusion cycles for any given membrane filter pore diameter (sample path shown in blue). Please click here to view a larger version of this figure.
2. Birefringence measurements of DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) and DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) polymolecular assemblies.
Figure 4: Schematic representation of the birefringence setup and connections for the optical signals. A) A superconducting electromagnet supplies a 5.5 T magnetic field. The light from a diode laser at 635 nm is polarized by two crossed polarizers. A photoelastic modulator PEM-90 operates at 50 KHz with an amplitude A0 of 2.405 rad and placed between the two polarizers. The sample lies in the magnet between the PEM and the second polarizer. Non-polarizing mirrors guide the light through the different elements and is finally detected by a photo detector. The first and second harmonic and
of the AC signal are monitored, permitting the calculation of the birefringence signal giving information on the magnetic alignability of the Ln3+ chelating polymolecular assemblies. The sample cuvette is connected to an external water bath for temperature control (blue). The temperature of the sample is monitored with a temperature probe (red). B) The signal from the photo detector is fed into a second order Sallen-Key low pass filter (24 V AC power supply) with a cut-off frequency of 360 Hz through a ±12 V DC power supply braded cable (3). The low pass filter extracts the DC component
and delivers it to the PC-interface (4) through a BNC 50 Ω cable. The signal from the photo detector is delivered to the two lock-in amplifiers (which extract the first and second harmonic
and
) through a BNC 50 Ω cable (1) & (2). The harmonic intensities are detected by a phase-sensitive detection. Consequently, the PEM signal is used as reference signal for the lock-in amplifiers (1f-output of the PEM into the first lock-in amplifier and 2f-output into the second, connected with BNC 50 Ω cables). The output signals are delivered to the PC-interface unit through BNC 50 Ω cables. Analog acquisition units cFP-AI-110 and cFP-CB-1 digitalize the signal that is transferred to the computer through a RS 232 cable for monitoring. The type K temperature probe is also connected to the PC-interface unit where analog acquisition units cFP-CB-3 and cFP-TC-120 digitalize the signal before transferring it to the computer through a RS 232 cable for monitoring. C) Picture of the schematic setup presented in B. Key elements are identified with corresponding numbers from 1 to 4. Please click here to view a larger version of this figure.
Figure 5: Illustrations of the employed settings and program screenshots. A) PEM settings: retardation 2.405 rad, wavelength 635 nm, frequency 50 Hz. White circles indicate what settings to be activated (USR = user defined retardation, LOC = local mode of operation). B) Lock-in amplifier settings. The sensitivity (1) has to be selected before each measurement as required in step 2.11. There should not be more than four red bars on the display (3) to avoid a signal overload. An overload occurs when the red led in (1) turns on, making a measurement impossible. Press the auto phase button (2) before every measurement. C) Screenshots of the program Tesla_Magnet_Const_V092 provided as supplementary information. The program allows control of the magnetic field and recording of all the signal outputs as a function of time. The magnetic field strength and sample temperature are plotted in (1). The first and second harmonic and
of the AC signal measured by the two lock-in amplifiers are plotted in (2). The intensity of the direct current
is plotted in (3). The retardation is calculated as described in step 2.13 and plotted in (4). The magnetic field strength is set in (5). The direct measurement of the temperature recorded by the Type K thermocouple is presented in (6) and the output signals (
and
) in (7). Additional sample information may be inserted in (8) such as the employed sensitivity of the amplifiers, sample name, etc. The data may be logged and exported to a .txt file provided in (9). Start and stop the data acquisition with the "START log" button (10). Please click here to view a larger version of this figure.
The birefringence signal of a non-extruded DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) sample was monitored under a 5.5 T magnetic field during a heating and cooling cycle from 5 to 40 °C and back at a rate of 1 °C/min (Figure 6). The birefringence results confirmed high magnetic alignments at 5 °C with a value of 1.5 x 10-5, twice as strong as for the reported extruded systems.6,7,23 The zeroing of the birefringence signal above the Tm of DMPC at 24 °C was caused by the formation of non-alignable vesicles. The movement appearance of the liquid disordered phase triggered major rearrangements in the polymolecular assemblies. These rearrangements are thermo-reversible. Alignable species were regenerated upon cooling below Tm and the birefringence signal followed the same trend as on heating. The distinct peaks occurring around Tm mark the replacement of the alignable assemblies by non-alignable vesicles.23 The slow kinetics of the molecular rearrangements with respect to the applied heating and cooling rate of 1 °C/min explain why the peaks were not overlapping. Instead, both peaks started at the Tm of DMPC, suggesting that the bilayer lipids must have a certain degree of order to favor the formation of alignable species.
Figure 6: Birefringence signal as a function of temperature for a non-extruded DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) sample upon heating (red) and cooling (blue) at 1 °C/min. The sample was prepared following the protocol steps 1 to 1.3.5. The birefringence measurements were conducted following the protocol step 2. The magnetic field strength was ramped up to 5.5 T and the sample was maintained at 5°, achieving a birefringence signal of 1.5 x 10-5 before proceeding to the heating and cooling cycle. The birefringence signal flatlines at temperatures above 35 °C where no alignment was observed as the sample was solely composed of vesicles. Upon cooling, the bicelles were regenerated and a final birefringence signal of 7.2 x 10-6 was achieved at 5.5 T and 5 °C. The magnetic field strength was ramped down to 0 T and the sample was maintained at 5 °C. Please click here to view a larger version of this figure.
A DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) sample was hydrated following the heating and cooling procedure in step 1.3.4 and subsequently extruded 10 times at 60 °C through membrane filters of different pore sizes, see step 1.4. At 60 °C, the lipid mixture assembles into vesicles, which are shaped by the extrusion process.16,35,36,37 After completing the extrusion, the bicelles were regenerated by cooling to 5 °C and the hydrodynamic diameter DH was measured by DLS. The magnetic alignability of the bicelles was evaluated at 5 °C by computing the Af with SANS at 8 T and by measuring the birefringence signal at 5.5 T; see Figure 7. The birefringence signal was obtained by ramping the field up to 5.5 T and back down to 0 T as shown in Figure 7A. The peak birefringence occurred at 5.5 T where the highest degree of alignment was expected according to equation 1. The hydrodynamic diameter DH of the bicelles was reduced to 220, 190, 106, and 91 nm by successive extrusions through membranes with pore sizes of 800, 400, 200, and 100 nm respectively. The corresponding decrease in magnetic alignment was confirmed by the decreasing birefringence signal and the reduction in absolute Af as it approached zero in Figure 7B. The results confirmed the possibility of controlling bicelle size and magnetic alignment through tailoring of the vesicles by extrusion at 60 °C and cooling back to 5 °C.
Figure 7: Magnetic alignment of a DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) sample extruded through membrane filters of various pore dimensions. A) Birefringence signal Δn′ as a function of the magnetic field strength B when ramping up and down for the sample extruded through 800 nm pores. The peak birefringence was reached at 5.5 T in accordance with equation 1. This maximal birefringence value is reported in B). The same sample was extruded through 400 nm pores. The magnetic alignment was evaluated by both birefringence measurements (black squares) at 5.5 T (analogously to what was done for the previous extrusion step in A) and by computation of alignment factors Af (red circles) at 8 T plotted as a function of the hydrodynamic diameter DH obtained by DLS. The magnetic alignment was evaluated analogously on the same sample extruded through 200 nm pores, and one last time after extruding through 100 nm pores. All measurements were performed at 5 °C. Please click here to view a larger version of this figure.
A detailed account of how birefringence measurements were used in combination with SANS experiments to evaluate methods for generating highly magnetically responsive Ln3+ chelating phospholipids assemblies is in Isabettini et al.23 The proposed fabrication protocols are also applicable for assemblies composed of the longer DPPC and DPPE-DTPA phospholipids or for those containing chemically engineered steroid derivatives in their bilayer.11,12,17,18,19 The only requirement being that the sample is heated to sufficiently high temperatures in steps 1.3.2, 1.3.3, 1.3.4 and 1.4.2. The temperatures must allow the bilayer lipids to enter a liquid disordered phase, guarantying optimal hydration of the dry lipid film or sample regeneration. DPPC/DPPE-DTPA/Tm3+ (molar ratio 4:1:1) assemblies, for example, need to be heated above the phase transition temperature of DPPC at 42 °C, while the analogous DMPC-based system must be heated above 24 °C. A sufficiently high temperature is also necessary to guarantee the formation of extrudable vesicles occurring when the lipid bilayer is in a disordered state in step 1.4. The freeze-thawing cycles in step 1.3.2 may be fully replaced by H&C cycles.23 However, the sample needs more time to fully hydrate the lipid film with this procedure and must be vortexed 20 min when at 5 °C and 2 min when at 60 °C. Additional H&C cycles are undertaken if elements of the dry lipid film are still observed on the glass walls of the flask.
The Tm3+ chelating bicelles presented in this protocol align perpendicular to the magnetic field direction. This alignment direction originates from the large positive magnetic susceptibility of Tm3+.11,14 Other lanthanide ions such as Dy3+ and Yb3+ may also be applied.11,13,19 The different magnetic anisotropy of the Ln3+ offers additional means of tailoring the magnetic alignment of the bicelles. For example, Dy3+ enhances the intrinsically negative magnetic susceptibility of the bilayer phospholipids, resulting in a high degree of alignment of the bicelles parallel to the magnetic field direction.13 This change in alignment direction is detected by a change in sign of both the birefringence signal and the alignment factors computed from anisotropic 2D SANS patterns. It is important to note that the magnetic susceptibility is not solely dictated by the chemical nature of the Ln3+ but by the chelate geometry of the Ln3+-phospholipid complex.19,38 The magnetic susceptibility may be engineered by synthesizing different Ln3+ chelating phospholipid headgroups, defining the magnetic response of the resulting assemblies.38
Every sample is optically different depending on the nature of the constituting lipids employed. Monitoring the sample's turbidity as a function of temperature is a complementary method to evaluate temperature-induced structural transformations in the assemblies. Although these measurements are usually conducted in the absence of a magnetic field in a spectrophotometer, monitoring the intensity of the laser's direct current with the setup proposed herein offers the same information in the presence of a magnetic field.11,16 The DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) samples are usually less turbid than their Chol-OH containing DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) counterparts at 5 °C. Samples resembling water at 5 °C are generally not alignable in a magnetic field. At room temperature, both samples look transparent because the DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) samples are in a transition phase between bicelles and vesicles and large concentric holes appear in the DMPC/Chol-OH/DMPE-DTPA/Tm3+ (molar ratio 16:4:5:5) bicelles.11,16,23 The transition state of bicelles to vesicles in DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) is also accompanied with an increase in the sample's viscosity at room temperature. This temperature-dependent change in turbidity makes choosing the right sensitivity in step 2.11 difficult. If the sensitivity is adjusted too high on a turbid sample at 5 °C, the more transparent nature of the sample on heating may cause an overload of the amplifiers. Moreover, highly turbid samples will considerably increase the noise to signal ratio and may not be suitable for birefringence measurements. The laser light must be able to go through the sample in order to be detected.
Non-extruded samples are always more turbid and have the tendency to aggregate upon short term storage in the fridge. Nevertheless, the magnetically responsive samples are readily regenerated with a H&C cycle. Non-extruded samples may also be stored in the frozen state and readily regenerated by H&C cycles. Extruded samples are kept in the fridge and commonly measured in one week following the sample's preparation. No studies report on the prolonged storage of extruded species in either a liquid or a frozen state. Therefore, the size distribution of the assemblies obtained from extrusion cannot be guaranteed over prolonged storage.
Analogously to any bicelle system, these magnetically alignable planar assemblies only exist in a defined range of lipid composition and concentration. Altering the lipid ratios will result in different assembly architectures, including the formation of micelles, ribbons, and vesicles.5,11,16,18,20 The phosphate buffer concentration and pH in step 1.1.3 plays a crucial role in shaping the bicelles and their magnetic response. The buffer defines the physico-chemical interactions governing the hydrophilic environment surrounding the polymolecular assemblies. Lower buffer concentrations result in different assembly architectures, whilst higher concentrations cause sample aggregation and precipitation due to an excess charge screening. Under acidic conditions with pH values between 3 and 4, the carboxylic acid moieties serving as ligands in the DMPE-DTPA/Ln3+ complex are protonated. This results in the destruction of the magnetically responsive polymolecular assemblies, observed by aggregation and precipitation in the sample. The magnetically responsive Ln3+ polymolecular assemblies have a reasonable resistance towards more basic pH values. However, DMPC/DMPE-DTPA/Tm3+ (molar ratio 4:1:1) bicelles were shown to break up into micelles at pH values of 12.9.11 The samples must never be exposed to tap water or other salts. Any other ion will disturb the Ln3+ chelating process or result in aggregation of the assemblies due to charge screening. For SANS measurements, the buffer is prepared as described in step 1.1.3 in D2O instead of ultrapure H2O. Note that the pH meter reading will be 7.0 (corresponding to a pD value of 7.4).
The structural transformations occurring in polymolecular assemblies subject to a heating and cooling cycle are thermo-reversible. Therefore, the final birefringence signal at 5 °C should be the same as before the temperature cycle.11,16 If the birefringence signal is higher after the cycle, the sample was not properly regenerated in step 1.3.4. This commonly occurs in samples stored for a prolonged period of time. A lower birefringence signal after the temperature cycle as observed in Figure 6 indicates a problem in the experimental setup. Most commonly, the laser light path was disturbed by back scattering or another object. This is especially problematic with the temperature probe inserted directly into the sample (see step 2.8) which should be placed as to not interfere with the direct path of the laser light. A disturbed light path causes a fall in the , a noisy signal, and/or abnormal peaks in the birefringence-temperature curves. For example, the peak occurring on heating at about 35 °C in Figure 6 was caused by expansion of the water-cooling tubes into the direct path of the laser light. The birefringence signal may not be trusted from that point onwards. Although the general shape of the cooling curve was normal, the lower birefringence signal obtained at 5 °C was caused by the interference.
The birefringence values obtained from following this protocol are not absolute and are used to compare samples amongst themselves. For comparison with literature values, a calibration with a reference system is required. For example, the sign of the measured retardation depends on the alignment of the set-up and may be checked with toluene, which has a Cotton-Mouton constant of 3.27 × 10−9 T−2.39,40
The birefringence signal originating from changes in the sample's magnetic alignment may be decoupled from the signal caused by molecular rearrangements in the bilayer. Alignment factors computed from anisotropic 2D SANS patterns obtained under a magnetic field are only influenced by the bulk alignment of the polymolecular assemblies. The two methods are complementary and allow decoupling of the contributions to the birefringence signal. The proposed birefringence setup could be perfected by splitting the laser beam, allowing for the simultaneous monitoring of samples with and without exposure to the external magnetic field. The birefringence results obtained for the sample in the magnetic field could be normalized by the signal obtained for the sample at 0 T, effectively accounting for the background.
Birefringence measurements are not limited to quantifying the magnetic alignment of bicelles. Numerous soft-materials generate a birefringence signal due to ordering of their internal structure. The proposed setup allows to monitor the birefringence of such materials as a function of temperature with or without an external magnetic field. Anthracene organogel fibers, wormlike micelles under flow, nanocrystalline cellulose and amyloid-Fe3O4 fibrils are a few examples whose birefringence behavior was successfully evaluated with the proposed setup.29,30,32,41
The authors have nothing to disclose.
The authors acknowledge the Swiss National Science Foundation for financing SMhardBi (project number 200021_150088/1). The SANS experiments were performed at the Swiss spallation neutron source SINQ, Paul Scherrer Instute, Villigen, Switzerland. The authors warmly thank Dr. Joachim Kohlbrecher for his guidance with the SANS experiments. The birefringence measurement setup under high magnetic fields was inspired from the existing setup at the high-field magnetic laboratory HFML, Nijmegen, The Netherlands. We thank Bruno Pfister for his help in developing the electronics of the birefringence setup, Jan Corsano and Daniel Kiechl for constructing the frameworks permitting fine and facile alignment of the laser, and Dr. Bernhard Koller for ongoing technical support.
1,2-dimyristoyl-sn-glycero-3-phosphocholine (DMPC) | Avanti Polar Lipids | 850345P | >99% |
1,2-dimyristoyl-sn-glycero-3-phospho-ethanolamine-diethylene triaminepentaacetate acid hexammonium salt (DMPE-DTPA) | Avanti Polar Lipids | 790535P | >99% |
Thulium(III) chloride | Sigma-Aldrich | 439649 | anhydrous, powder, 99.9% trace metals basis |
Dysprosium(III) chloride | Sigma-Aldrich | 325546 | anhydrous, powder, 99.9% trace metals basis |
Ytterbium(III) chloride | Sigma-Aldrich | 439614 | anhydrous, powder, 99.9% trace metals basis |
Chloroform | Sigma-Aldrich | 319988 | contains ethanol as stabilizer, ACS reagent, ≥99.8% |
Methanol | Sigma-Aldrich | 34860 | ≥99.9% |
Cholesterol | Amresco | 433 | Ultra pure grade |
D2O | ARMAR chemicals | 1410 | 99.8 atom % D |
Ultrapure water | Millipore | Synergy pak2 (SYPK0SIX2), Millipack GP (MPGP02001) | |
electronic pH meter | Metrohm | 17440010 | |
Whatmann Nuclepore 25 mm 100nm membrane filter | VWR | 515-2028 | |
Whatmann Nuclepore 25 mm 200nm membrane filter | VWR | 515-2029 | |
Whatmann Nuclepore 25 mm 400nm membrane filter | VWR | 515-2030 | |
Whatmann Nuclepore 25 mm 800nm membrane filter | VWR | 515-2032 | |
Whatmann Filter paper | VWR | 230600 | |
25 ml round bottom flask | VWR | 201-1352 | 14/23 NS |
3 ml glass snap-cup | VWR | 548-0554 | ND18, 18x30mm |
2.5 ml glass syringe | Hamilton | ||
Sodium dihydrogen phosphate dihydrate | Merk | 1.06342 | Salt used to make phosphate buffer |
di-Sodium hydrogen phosphate | Merk | 1.06586 | Salt used to make phosphate buffer |
Liquid Nitrogen | Carbagas | – | |
Pressurized Nitrogen gas | Carbagas | – | 200 bar bottle |
Lipid Extruder 10 ml | Lipex | – | Fully equipped with thermobarrel |
High-pressure PVC tube | GR NETUM | – | must resist more than 4 MPa |
Serto adaptors | Sertot | – | |
Nitrile gloves | VWR | – | |
2 ml glass pipettes | VWR | 612-1702 | 230 mm long |
Diode Laser | Newport | LPM635-25C | |
DSP Dual Phase Lock-in Amplifier | SRS | SR830 | |
Photodiode Detector | Silonex Inc. | SLSD-71N5 | 5mm2, Silicon, photo-conductive |
5.5 T Cryogenic Magnetic | Cryogenic/Oerlikon AG | – | 12 bar He-cooled. RW4000/6000 compressor, RGD 5/100 TA cryo-head |
Second order low pass filter | home-built | – | Linear power supply 24V DC, second order, Sallen Key, cut-off frequency 360 Hz, +/- 12V, max 10 mA |
Photoelastic modulator | Hinds instruments | PEM-90 | |
Glan-Thompson Calcite Polarizer | Newport | 10GT04 | 25.4mm diameter |
Quartz sample cuvette | Hellma | 165-10-40 | temperature controlled cell, 0.8 ml, 10mm path length |
Temperature probe | Thermocontrol | – | Type K, 0.5mm diameter, Thermocoax |
Non-polarizing mirrors | Newport | 50326-1002 | 25.4mm |
RS 232 cables | National Instruments | 189284-02 | For Connecting to the RS-232 Port on the front of Compact FieldPoint Controllers |
BNC 50 Ω cable and connectors | National Instruments | 763389-01 | |
cFP-AI-110 | National Instruments | 777318-110 | 8-Channel Analog Voltage and Current Input Module for Compact FieldPoint |
cFP-CB-1 | National Instruments | 778618-01 | Integrated Connector Block for Wiring to Compact FieldPoint I/O |
cFP-CB-3 | National Instruments | 778618-03 | Integrated Isothermal Connector Block for Wiring Thermocouples to the cFP-TC-120 Module |
cFP-TC-120 | National Instruments | 777318-120 | 8-Channel Thermocouple Input Module for Compact FieldPoint |
cFP-1804 | National Instruments | 779490-01 | Ethernet/Serial Interface for NI Compact FieldPoint |
LabView 2010 | National Instruments | – | |
Industrial power supply | Traco Power | TCL 060-124 | 100-240V AC |
Waterbath | Julabo | FP40-HE | refrigerated/Heating Circulator |