This video demonstrates the self-assembly of amyloid peptides into a beta sheet-rich supramolecular structure using Fourier transform infrared spectroscopy. An infrared beam is passed through a crystal with a high refractive index, and energy absorption across the interface of the crystal and the sample is recorded. The secondary structures of the sample proteins are identified by analyzing their characteristic absorption peaks at specific regions of the infrared spectrum, which aids in identifying the formation of the supramolecular assembly.
Protocol
1. Characterization of Supramolecular Self-Assembly Structures
Formation of Amyloid Fibers
To prepare a self-assembly solution, weigh out 1 mg of the peptide powder using an analytical balance. Dissolve into a mixture (pH 7.5) of 20% acetonitrile and 10 mM (4-(2-hydroxyethyl)-1-piperazineethanesulfonic acid (HEPES) in a 1.5 mL microcentrifuge tube, to a final concentration of 1 mg/mL peptide assembly mixture. Vortex the assembly solution and leave it to assemble at room temperature.
Spectroscopic Characterization of Amyloid Fibers
Follow the peptide assembly process via Fourier-transform infrared (FTIR) spectroscopy every few days. A broad peak centered around 1670 cm-1 is the IR signature arising from unassembled peptides in the sample. The peptide assembly samples usually take one to two weeks for the broad unassembled peak to disappear and reach maturation.
Dry an aliquot of 8-10 μL of the assembly solution as a thin film on the ATR diamond crystal. Monitor the disappearance of a large and broad water peak from 1640 to 1630 cm-1 as the dry film forms.
Acquire IR spectra from 1500-1800 cm-1 averaging 50 scans with a 2 cm-1 resolution. Acquire and subtract the background scans prior to each sample scan. The IR signature for β-sheet assembly is a sharp peak between 1625 and 1635 cm-1 (Figure 1A).
Representative Results
Figure 1. Supramolecular characterization of 1,2-dithiolane modified peptide. (A) FT-IR of 1 mg/mL 1,2-dithiolane-KLVFFAQ-NH2 fibers assembled in 10mM HEPES, pH 7.5 in 20% CH3CN. The peak at 1627 cm-1 is consistent with the peptides assembled in a β-sheet conformation. (B) CD of 1 mg/mL 1,2-dithiolane-KLVFFAQ-NH2 fibers assembled in 10 mM HEPES, pH 7.5 in 20% CH3CN. The ellipticity minimum at 218 nm is consistent with the peptides assembled in a β-sheet conformation. (C) Image of the 1,2-dithiolane-KLVFFAQ-NH2 amyloid fiber (negative stain of 2% uranyl acetate) by TEM. Scale bar is 100 nm.
Divulgations
The authors have nothing to disclose.
Materials
Acetonitrile
Fisher Scientific
A998-4
Flammable; irritating to eyes; Use personal protective equipment; Use only under a fume hood; keep away from open flame or hot surface; if contacted rinse wiith water for at least 15 minutes and obtain medical attention