Monoliti Microhoneycomb preparati dalla liofilizzazione unidirezionale di cellulosa nanofibra basato Sols: metodo ed estensioni
Un abonnement à JoVE est nécessaire pour voir ce contenu. Connectez-vous ou commencez votre essai gratuit.
1Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen,Tsinghua University, 2School of Materials Science and Engineering,Tsinghua University, 3Institute of Multidisciplinary Research for Advanced Materials,Tohoku University, 4Tsinghua-Berkeley Shenzhen Institute (TBSI),Tsinghua University, 5School of Chemical Engineering and Technology,Tianjin University
Chapitres
- 00:04Titre
- 00:57Preparation of 1 wt% (2,2,6,6-Tetramethylpiperidin-1-yl) oxyl (TEMPO)-mediated Oxidized Cellulose Nanofiber (TOCN) Sol
- 04:01Preparation of TOCN-TiO2 and TOCN-surface-oxidized Carbon Fiber (SOCF) Mixed Sols
- 04:59Microhoneycomb Monolith (MHM) Preparation from 1 Wt% TOCN Sol (MHM-TOCN) or TOCN Mixed Sols (MHM-TOCN/SBR, MHM-TOCN/TiO2, MHM-TOCN/SOCF)
- 06:54Results: Morphologies of the MHM-TOCN, MHM-TOCN/SBR, MHM-TOCN/TiO2, and MHM-TOCN/SOCF
- 08:39Conclusion
Qui, presentiamo un protocollo generale per preparare una varietà di microhoneycomb monoliti (MHMs) in cui il liquido può passare attraverso con una caduta di pressione estremamente bassa. MHMs ottenuti dovrebbero essere utilizzati come filtri, supporti di catalizzatore, flusso-tipo di elettrodi, sensori e ponteggi per biomateriali.