Full-field Strain Measurements for Microstructurally Small Fatigue Crack Propagation Using Digital Image Correlation Method

Please note that all translations are automatically generated. Click here for the English version.

全視野ひずみ測定における微視組織的微小疲労き裂の伝ぱデジタル画像相関法を用いた

DOI:

10.3791/59134-v

•

07:37 min

•

January 16, 2019

•

Evgenii Malitckii, Heikki Remes, Pauli Lehto, Sven Bossuyt

¹Department of Mechanical Engineering,Aalto University School of Engineering

Chapitres

00:00Titre
01:54Specimen Preparation and Annealing
02:49Fatigue Pre-cracking
03:21Microstructural Characterization
03:53Decoration with a Pattern
04:54Results Analysis
05:36Representative Results
06:49Conclusion

Summary

Traduction automatique

亜粒レベルで累積的な変形場を明らかにするき裂成長速度測定場とひずみ場解析を組み合わせた新しい方法論的アプローチを用いた微視組織的微小疲労き裂の成長挙動を調べた。

Tags

Keywords: Digital Image Correlation Full-field Strain Measurement Microstructurally Small Fatigue Crack Propagation Lightweight Solutions Advanced Steel Materials Structural Analysis Wave Induced Loading Welded Joints Fatigue Small Fatigue Crack Initiation Annealing Grain Size Electron Back Scatter Diffraction

Article

Embed

AJOUTER À LA PLAYLIST

Usage Statistics

Vidéos Connexes

同時定量伝導率およびAFMを用いた有機太陽電池材料の機械的特性の測定

1〜2平面フロー小角中性子散乱を用いた材料の微細構造の下で流量を測定

重度不足減衰フリンジフィールド静電MEMSアクチュエータに時間改善スイッチング用リアルタイムDC-ダイナミックバイアス方式

サンプリングモアレ縞からのマイクロ/ナノスケールひずみ分布測定

超音波疲労引張圧縮モードでのテスト

連結を解くコリオリの力と全視野熱回転浮力の影響回転チャネルのプロパティを転送します。

マイクロ波光伝導減衰法による半導体中のキャリアライフタイム測定

デジタル画像相関法と中間ひずみ率材料解析

デジタル画像相関を用いた溶接試料の共振疲労試験における亀裂モニタリング

無線周波数伝搬チャネルにおける測定のためのベクトルネットワークアナライザのキャリブレーション

Read Article