Organic Structure-directing Agent-free Synthesis for *BEA-type Zeolite Membrane

Please note that all translations are automatically generated. Click here for the English version.

유기 구조 지시 에이전트 무료 합성 *BEA 형 제올라이트 멤브레인

DOI:

10.3791/60500-v

•

08:49 min

•

February 22, 2020

•

Motomu Sakai, Noriyuki Yasuda, Yuto Tsuzuki, Masahiko Matsukata^2,3

¹Research Organization for Nano & Life Innovation,Waseda University, ²Department of Applied Chemistry,Waseda University, ³Advanced Research Institute for Science and Engineering,Waseda University

Chapitres

00:05Introduction
00:41Support Preparation
01:22*BEA Seed Crystal Synthesis
03:59Seeding on Support by Dip-coating
05:34*BEA Membrane Preparation by a Secondary Growth Method
07:23Results: XRD and FE-SEM
08:22Conclusion

Summary

Traduction automatique

*BEA 종자 결정은 딥 코팅 방법에 의해 다공성 α-Al₂_O3 지지체상에 적재되었고, 유기 구조 지시제를 사용하지 않고 수열로 성장하였다. 결함이 거의 없는 *BEA형 제올라이트 멤브레인은 이차 성장 방법에 의해 성공적으로 제조되었다.

Tags

Zeolite Membrane BEA-type Zeolite Organic Structure-directing Agent-free Synthesis Alpha Aluminum Oxide Support Colloidal Silica Tetraethylammonium Hydroxide Sodium Hydroxide Sodium Aluminate Crystallization Teflon-lined Autoclave Vacuum Filtration

Article

Embed

AJOUTER À LA PLAYLIST

Usage Statistics

Vidéos Connexes

합성, 세포 전달 및<em> 생체 내</em> 덴드리머 기반 pH 센서의 응용 프로그램

콜드 입구 시스템 및 전자 충격 질량 분석법을 사용하여 휘발성 및 산화에 민감한 화합물의 분석

기능화의 합성 및 특성 금속 - 유기 프레임 워크

Synthesis and Characterization of Supramolecular Colloids

단일 분자 수준에서 순환 고분자의 합성 및 용융 상태에서 그들의 확산 운동의 특성

수용성 유기 금속 복합 어레이의 합성

Microfluidic 기반 CODMs의 합성 : COF 섬유의 지속적인 생산과 표면의 직접 인쇄를위한 도구

O-Carboxyanhydrides Ni/Zn 단지 중재의 Photoredox 반지 개통 중 합 제어

α, β-불포화 화합물 및 알킨스의 Persulfate-승진 벤젠내화를 통해 물에서 다기능화 벤젠의 효율적인 합성

생물학적 장벽의 침투 강화를 위한 순환 세포 침투 펩타이드의 구성

Read Article