Please note that all translations are automatically generated. Click here for the English version.
Ingegneria

Gleichzeitige Multi-Oberfläche Anodizations und Treppe-wie umgekehrte Vorurteile Ablösung der anodische Aluminium Oxide in Schwefelsäure und Oxalsäure-Elektrolyten

Published: October 05, 2017
doi:
10.3791/56432
, , , ,
1School of Advanced Materials Science and Engineering,Sungkyunkwan University, 2Department of Applied Organic Materials Engineering,Inha University

Summary

Ein Protokoll für die Herstellung von nanoporösen anodische Aluminium Oxide über gleichzeitige Multi-Oberflächen-Anodisierung gefolgt von Treppe-wie umgekehrte Vorurteile Abteilungen präsentiert. Es kann immer wieder die gleichen Aluminium-Substrat, präsentiert eine leichtfertige, High-Yield-und ökologisch saubere Strategie angewendet werden.

Abstract

Nach der Berichterstattung über die zweistufige Anodisierung, nanoporöse anodische Aluminium Oxide (AAOs) haben verwendet worden, weit in den vielseitigen Bereichen Grundlagenwissenschaften und industrielle Anwendungen aufgrund ihrer periodische Anordnung von Nanoporen mit relativ hohen Seitenverhältnis. Jedoch die Techniken gemeldet, so weit die könnte nur gültig für Mono-Oberfläche Anodisierung, zeigen entscheidende Nachteile, d. h., zeitaufwendig sowie komplizierte Verfahren, dass giftige Chemikalien und verschwenden wertvollen natürliche Ressourcen . In diesem Beitrag zeigen wir Ihnen eine einfache, effiziente und umweltfreundliche Methode zur nanoporöse AAOs in Schwefelsäure und Oxalsäure sauren Elektrolyten, fabrizieren, die Überwindung der Grenzen, die durch konventionelle AAO Herstellung Methoden entstehen können. Erste, plural AAOs entstehen auf einmal durch gleichzeitige Multi-Oberflächen-Anodisierung (SMSA), Mass-producibility der AAOs mit vergleichbaren Eigenschaften angibt. Zweitens können jene AAOs aus Aluminium (Al) Substrat getrennt werden durch die Anwendung der Treppe-wie umgekehrte Vorurteile (SRBs) in den gleichen Elektrolyten verwendet für die SMSAs, was bedeutet Einfachheit und grün technologische Eigenschaften. Schließlich kann eine Einheit Sequenz bestehend aus SMSAs, die nacheinander in Kombination mit SRBs basierende Ablösung wiederholt auf den gleichen Al-Substrat angewendet werden verstärkt die Vorteile dieser Strategie und auch garantiert die effiziente Nutzung der natürlichen Ressourcen.

Introduction

AAOs, die sich gebildet hatten, durch Eloxieren Al Substrat in einem sauren Elektrolyten haben stieß auf großes Interesse in diversen grundlegende Wissenschaft und Industrie, z. B. harte Vorlagen für Nanoröhren/Nanodrähte1,2,3 , 4 , 5, Energie-Speicher-Geräte6,7,8,9, Bio-sensing10,11, Filterung Anwendungen12,13 , 14, Masken für verdampfen und/oder Ätzen15,16,17und kapazitive Feuchte Sensoren18,19,20,21 ,22, aufgrund ihrer selbst bestellten Wabenstruktur, hohes Aspektverhältnis der Nanoporen und hervorragenden mechanischen Eigenschaften23. Für diese verschiedenen Anwendungen nanoporöse AAOs zuweisen, sollte sie freistehende Formen mit einem hoch und weiträumige geordnetes Array von Nanoporen. In diesem Zusammenhang Strategien für den Erhalt der AAOs (Eloxieren) Bildung und Trennung (abnehmen) Verfahren zu berücksichtigen.

In der Sicht der AAO-Formation war milde Anodisierung (nachfolgend als MA) etabliert unter Schwefelsäure, Oxalsäure und Phosphor-sauren Elektrolyten23,24,25,26 ,27. Jedoch stellte MA Prozesse niedrige Erträge der AAO Fertigung aufgrund ihres langsamen Wachstumsrate abhängig von relativ geringen Intensitäten der anodische Spannungen, die durch MA Schritten zur Verbesserung der Nanoporen Periodizität28 weiter verschlechtern würde ,29. So wurden harte Anodisierung (HA) Techniken als Alternativen Ma vorgeschlagen, durch die Anwendung höherer anodische Spannungen (Oxalsäure/schweflige Säure Elektrolyt) oder mittels konzentrierter Elektrolyt (Phosphorsäure)30,31, 32,33,34,35,36,37,38,39,40. HA zeigen Prozesse deutlichen Verbesserungen der Wachstumsraten sowie regelmäßige Arrangements, während resultierende AAOs wurde brüchiger, und die Dichte der Nanoporen waren reduzierten30. Darüber hinaus ist eine teure Kühlsystem erforderlich zur Ableitung Joules Erwärmung durch hohe Stromdichte31. Diese Ergebnisse beschränken die mögliche Anwendbarkeit der AAOs über HA-Prozesse.

Für die entsprechende Oberfläche von Al-Platte ein AAO trennt, wurde gezielte chemische Ätzung des verbleibenden Al Substrats am häufigsten genutzt von den MA und HA Prozesse mit giftigen Chemikalien, wie z. B. Kupferchlorid35,39 ,41,42 oder Quecksilber-Chlorid16,17,43,44,45,46, 47 , 48 , 49. jedoch diese Methode induziert nachteilige Nebenwirkungen, z.B., eine längere Reaktionszeit proportional zur restlichen Dicke der Al, Verschmutzung der AAO von Schwermetall-Ionen, schädliche Rückstände zu menschlichen Körper/natürliche Umgebungen , und ineffiziente Nutzung der wertvollen Ressourcen. Daher wurden viele Versuche unternommen, für direkte Ablösung der ein AAO zu realisieren. Obwohl kathodischen Spannung Delamination50,51 und anodische Spannung Ablösung7,41,42,52, Puls 53,54,55 präsentieren einen Verdienst, das die restlichen Al Substrat wiederverwendet werden kann, die ehemalige Technik fast vergleichbar mit denen in chemische Ätzung Methoden50dauert. Trotz deutliche Reduzierung der Bearbeitungszeit schädliche und hochreaktive Chemikalien/Beispiele Butanedione oder Perchlorsäure, dienten als Elektrolyte in der letztgenannten Techniken55, abnehmen, wo eine zusätzliche Reinigung Verfahren ist wegen der wechselnden Elektrolyt zwischen trennen und Eloxal-Verfahren erforderlich. Vor allem Einfluss auf die trennen Verhaltensweisen und Qualität der freistehende AAOs stark die Dicke. Im Falle der AAO mit relativ dünner Stärke könnte die freistehende Risse und/oder Öffnungen enthalten.

Alle oben aufgeführten experimentelle Ansätze wurden auf eine “Single-Oberfläche” der Al-Probe, ohne Oberfläche schützen technische Zwecke, und diese Funktion der konventionellen Technologien Exponate kritischen Einschränkungen der AAO Fabrikation angewendet in Bezug auf Ertrag sowie Verarbeitbarkeit beeinflusst das auch die mögliche Anwendbarkeit der AAOs56,57.

Um den steigenden Anforderungen in der AAO zusammenhängenden Bereichen in Bezug auf facile, ertragreich und grüne technologische Ansätze gerecht zu werden, hatten wir zuvor SMSA und direkte Ablösung durch SRBs unter Schwefelsäure56 und Oxalsäure57 Säure Elektrolyt, beziehungsweise. Es ist eine wohlbekannte Tatsache, dass plural AAOs auf mehrere Flächen in sauren Elektrolyten getaucht Al-Substrat gebildet werden können. SRBs, ein ausschlaggebender Unterschied unserer Methoden ermöglichen die Ablösung des jene AAOs von den entsprechenden Multi-Oberflächen des Al-Substrat in den gleichen sauren Elektrolyten verwendet für die SMSAs angibt, Massenproduktion, Einfachheit und technologischen grün Eigenschaften. Wir möchten darauf hinweisen, dass SRBs basierende Ablösung eine optimale Strategie für plural AAOs ist, hergestellt durch SMSAs56,57 und sogar gültig für relativ dünner Wandstärken der AAOs57 im Vergleich zu kathodischen Delamination (d.h., konstante reverse Bias) auf Single-Oberflächef “> 51. Schließlich eine Einheit Sequenz bestehend aus SMSAs, die nacheinander in Kombination mit SRBs basierende Ablösung kann auf dem gleichen Al-Substrat, Vermeidung von komplizierten Verfahren und giftig/reaktiven Chemikalien, welche die Vorteile der verstärkt wiederholt angewendet werden unsere Strategien und auch garantiert die effiziente Nutzung der natürlichen Ressourcen.

Protocol

Bitte beachten Sie alle damit verbundenen Materialien Sicherheitsdatenblätter (SDB) vor Beginn. Trotz der Öko-Natur dieses Protokolls ein paar Säuren und Oxidationsmitteln in die entsprechenden Verfahren eingesetzt. Darüber hinaus verwenden alle die richtige persönliche Schutzausrüstung (Kittel, Handschuhe, Schutzbrille, etc.). 1. Vorbereitung der Lösung Hinweis: nach vollständige Abdichtung des Schiffes Lösung-haltigen, kräftige magnetische rüh…

Representative Results

Flussdiagramm von nth AAO Sequenz hauptsächlich bestehend aus zweistufigen SMSAs, SRBs-Ablösung, Herstellung und verwandte chemische Ätzung präsentierte sich schematisch in Abbildung 1a. Jeder Einschub zeigen ein Rasterelektronenmikroskop (REM) Bild der Morphologie der entsprechenden Oberfläche auf jede einzelne Prozedur und ein Foto sofort nach der SRBs-Ablösung. Eine schematische Darstellung, nachdem die insgesamt 5th Wi…

Discussion

In diesem Papier haben wir erfolgreich eine facile, ertragreich und umweltfreundliche Methode zu fabrizieren nanoporöse AAOs durch SMSA und SRBs-Abteilung, die auf dem gleichen Al-Substrat für die Verbesserung der deutlich Mass-producibility als wiederholt werden könnte sowie die Nutzbarkeit der begrenzten natürlichen Ressourcen. Wie das Flussdiagramm Abbildung 1azeigt, unsere AAO Herstellung Strategie die herkömmliche zweistufige Anodisierung beruht auf Multi-Oberflächen Situation ge?…

Divulgazioni

The authors have nothing to disclose.

Acknowledgements

Die Autoren haben nichts preisgeben.

Materials

Sulfuric Acid >98% DUKSAN reagent 5950
Oxalic Acid Anhydrous, 99.5-100.2% KANTO chemical 31045-73
Phosphoric Acid, 85% SAMCHUN chemical P0463
Perchloric Acid, 60% SAMCHUN chemical P0181 Highly Reactive
Chromium(VI) Oxide Sigma Aldrich 232653 Strong Oxidizer
Ethanol, 95% SAMCHUN chemical E0219
Absolute Ethanol, 99.9% SAMCHUN chemical E1320
Double Jacket Beaker iNexus 27-00292-05
Low Temperature Bath Circulator JEIO TECH AAH57052K
Programmable DC Power Supply PNCYS EDP-3001 
Aluminum Plate, >99.99% Goodfellow
Platinum Cylinder Whatman 444685
Pure & Ultra Pure Water System (Deionized Water) Human Science Pwer II & HIQ II
DOWNLOAD MATERIALS LIST

Riferimenti

  1. Hong, Y. K., et al. Tuning and enhancing photoluminescence of light-emitting polymer nanotubes through electron-beam irradiation. Adv. Funct. Mater. 19 (4), 567-572 (2009).
  2. Hong, Y. K., et al. Fine Characteristics Tailoring of Organic and Inorganic Nanowires Using Focused Electron-Beam Irradiation. Angew. Chem. Int. Ed. 50 (16), 3734-3738 (2011).
  3. Lee, J. H., et al. Iron-gold barcode nanowires. Angew. Chem. Int. Ed. 46 (20), 3663-3667 (2007).
  4. Qin, L., Banholzer, M. J., Millstone, J. E., Mirkin, C. A. Nanodisk codes. Nano Lett. 7 (12), 3849-3853 (2007).
  5. Park, D. H., Kim, M. S., Joo, J. Hybrid nanostructures using π-conjugated polymers and nanoscale metals: synthesis, characteristics, and optoelectronic applications. Chem. Soc. Rev. 39 (7), 2439-2452 (2010).
  6. Ahn, Y. K., et al. Enhanced electrochemical capabilities of lithium ion batteries by structurally ideal AAO separator. J. Mater. Chem. A. 3 (20), 10715-10719 (2015).
  7. Chen, J., Wang, S., Ding, L., Jiang, Y., Wang, H. Performance of through-hole anodic aluminum oxide membrane as a separator for lithium-ion battery. J. Membr. Sci. 461, 22-27 (2014).
  8. Gao, Y., et al. Three-dimensional nanotube electrode arrays for hierarchical tubular structured high-performance pseudocapacitors. Nanoscale. 8 (27), 13280-13287 (2016).
  9. Hu, J., et al. Dual-template ordered mesoporous carbon/Fe2O3 nanowires as lithium-ion battery anodes. Nanoscale. 8 (26), 12958-12969 (2016).
  10. Kim, K., et al. Externally controlled drug release using a gold nanorod contained composite membrane. Nanoscale. 8 (23), 11949-11955 (2016).
  11. Poplausks, R., et al. Electrochemically etched sharp aluminium probes with nanoporous aluminium oxide coatings: Demonstration of addressed DNA delivery. RSC Adv. 4 (89), 48480-48485 (2014).
  12. Chen, X., Qiu, M., Ding, H., Fu, K., Fan, Y. A reduced graphene oxide nanofiltration membrane intercalated by well-dispersed carbon nanotubes for drinking water purification. Nanoscale. 8 (10), 5696-5705 (2016).
  13. Dervin, S., Dionysiou, D. D., Pillai, S. C. 2D nanostructures for water purification: graphene and beyond. Nanoscale. 8 (33), 15115-15131 (2016).
  14. Han, K., Heng, L., Wen, L., Jiang, L. Biomimetic heterogeneous multiple ion channels: a honeycomb structure composite film generated by breath figures. Nanoscale. 8 (24), 12318-12323 (2016).
  15. Kim, J., Kim, Y. H., Choi, S. H., Lee, W. Curved Silicon Nanowires with Ribbon-like Cross Sections by Metal-Assisted Chemical Etching. ACS Nano. 5 (6), 5242-5248 (2011).
  16. Zeng, Z., et al. Fabrication of Graphene Nanomesh by Using an Anodic Aluminum Oxide Membrane as a Template. Adv. Mater. 24 (30), 4138-4142 (2012).
  17. Lim, N., et al. A tunable sub-100 nm silicon nanopore array with an AAO membrane mask: reducing unwanted surface etching by introducing a PMMA interlayer. Nanoscale. 7 (32), 13489-13494 (2015).
  18. Zhang, J., Liu, X., Neri, G., Pinna, N. Nanostructured Materials for Room-Temperature Gas Sensors. Adv. Mater. 28 (5), 795-831 (2016).
  19. Blank, T. A., Eksperiandova, L. P., Belikov, K. N. Recent trends of ceramic humidity sensors development: A review. Sens. Actuators B. 228, 416-442 (2016).
  20. Kim, Y., et al. Capacitive humidity sensor design based on anodic aluminum oxide. Sens. Actuators B. 141 (2), 441-446 (2009).
  21. Mahboob, M. R., Zargar, Z. H., Islam, T. A sensitive and highly linear capacitive thin film sensor for trace moisture measurement in gases. Sens. Actuators B. 228, 658-664 (2016).
  22. Sharma, K., Islam, S. S. Optimization of porous anodic alumina nanostructure for ultra high sensitive humidity sensor. Sens. Actuators B. 237, 443-451 (2016).
  23. Lee, W., Park , S. J. Porous Anodic Aluminum Oxide: Anodization and Templated Synthesis of Functional Nanostructures. Chem. Rev. 114 (15), 7487-7556 (2014).
  24. Keller, F., Hunter, M., Robinson, D. Structural features of oxide coatings on aluminum. J. Electrochem. Soc. 100 (9), 411-419 (1953).
  25. Diggle, J. W., Downie, T. C., Goulding, C. W. Anodic oxide films on aluminum. Chem. Rev. 69 (3), 365-405 (1969).
  26. O’Sullivan, J. P., Wood, G. C. The Morphology and Mechanism of Formation of Porous Anodic Films on Aluminium. Proc. R. Soc. London A. 317 (1531), 511-543 (1970).
  27. Thompson, G. E., Wood, G. C. Porous anodic film formation on aluminium. Nature. 290 (5803), 230-232 (1981).
  28. Masuda, H., Fukuda, K. Ordered Metal Nanohole Arrays Made by a Two-Step Replication of Honeycomb Structures of Anodic Alumina. Science. 268 (5216), 1466-1468 (1995).
  29. Masuda, H., Satoh, M. Fabrication of Gold Nanodot Array Using Anodic Porous Alumina as an Evaporation Mask. Jpn. J. Appl. Phys. 35 (1B), L126-L129 (1996).
  30. Chu, S. Z., Wada, K., Inoue, S., Isogai, M., Yasumori, A. Fabrication of Ideally Ordered Nanoporous Alumina Films and Integrated Alumina Nanotubule Arrays by High-Field Anodization. Adv. Mater. 17 (17), 2115-2119 (2005).
  31. Lee, W., Ji, R., Gösele, U., Nielsch, K. Fast fabrication of long-range ordered porous alumina membranes by hard anodization. Nature Mater. 5 (9), 741-747 (2006).
  32. Li, Y., Zheng, M., Ma, L., Shen, W. Fabrication of highly ordered nanoporous alumina films by stable high-field anodization. Nanotechnology. 17 (20), 5101-5105 (2006).
  33. Li, Y. B., Zheng, M. J., MA, L. High-speed growth and photoluminescence of porous anodic alumina films with controllable interpore distances over a large range. Appl. Phys. Lett. 91 (7), 073109 (2007).
  34. Lee, W., et al. Structural engineering of nanoporous anodic aluminium oxide by pulse anodization of aluminium. Nature Nanotech. 3 (4), 234-239 (2008).
  35. Li, Y., Ling, Z. Y., Chen, S. S., Wang, J. C. Fabrication of novel porous anodic alumina membranes by two-step hard anodization. Nanotechnology. 19 (22), 225604 (2008).
  36. Schwirn, K., et al. Self-Ordered Anodic Aluminum Oxide Formed by H2SO4 Hard Anodization. ACS Nano. 2 (2), 302-310 (2008).
  37. Yao, Z., Zheng, M., MA, L., Shen, W. The fabrication of ordered nanoporous metal films based on high field anodic alumina and their selected transmission enhancement. Nanotechnology. 19 (46), 465705 (2008).
  38. Lee, W., Kim, J. C., Cösele, U. Spontaneous Current Oscillations during Hard Anodization of Aluminum under Potentiostatic Conditions. Adv. Funct. Mater. 20 (1), 21-27 (2010).
  39. Yi, L., Zhiyuan, L., Shuoshuo, C., Xing, H., Xinhua , H. Novel AAO films and hollow nanostructures fabricated by ultra-high voltage hard anodization. Chem. Commun. 46 (2), 309-311 (2010).
  40. Kim, M., Ha, Y. C., Nguyen, T. N., Choi, H. Y., Kim, D. Extended self-ordering regime in hard anodization and its application to make asymmetric AAO membranes for large pitch-distance nanostructures. Nanotechnology. 24 (50), 505304 (2013).
  41. Chen, W., Wu, J. S., Yuan, J. H., Xia, X. H., Lin, X. H. An environment-friendly electrochemical detachment method for porous anodic alumina. J. Electroanal. Chem. 600 (2), 257-264 (2007).
  42. Gao, L., Wang, P., Wu, X., Yang, S., Song, X. A new method detaching porous anodic alumina films from aluminum substrates. J. Electroceram. 21 (1-4 SPEC), 791-794 (2008).
  43. Asoh, H., Nishio, K., Nakao, M., Tamamura, T., Masuda, H. Conditions for Fabrication of Ideally Ordered Anodic Porous Alumina Using Pretextured Al. J. Electrochem. Soc. 148 (4), B152-B156 (2001).
  44. Wu, M. T., Hon Leu, I. C., H, M. Effect of polishing pretreatment on the fabrication of ordered nanopore arrays on aluminum foils by anodization. J. Vac. Sci. Technol., B. 20 (3), 776-782 (2002).
  45. Asoh, H., Ono, S., Hirose, T., Nakao, M., Masuda, H. Growth of anodic porous alumina with square cells. Electrochim. Acta. 48 (20-22), 3171-3174 (2003).
  46. Masuda, H., et al. Ordered Mosaic Nanocomposites in Anodic Porous Alumina. Adv. Mater. 15 (2), 161-164 (2003).
  47. Chu, S. Z., et al. Large-Scale Fabrication of Ordered Nanoporous Alumina Films with Arbitrary Pore Intervals by Critical-Potential Anodization. J. Electrochem. Soc. 153 (9), B384-B391 (2006).
  48. Byun, J., Lee, J. I., Kwon, S., Jeon, G., Kim, J. K. Highly Ordered Nanoporous Alumina on Conducting Substrates with Adhesion Enhanced by Surface Modification: Universal Templates for Ultrahigh-Density Arrays of Nanorods. Adv. Mater. 22 (18), 2028-2032 (2010).
  49. Gong, J., Butler, W. H., Zangari, G. Tailoring morphology in free-standing anodic aluminium oxide: Control of barrier layer opening down to the sub-10 nm diameter. Nanoscale. 2 (5), 778-785 (2010).
  50. Schneider, J. J., Engstler, J., Budna, K. P., Teichert, C., Franzka, S. Freestanding, highly flexible, large area, nanoporous alumina membranes with complete through-hole pore morphology. Eur. J. Inorg. Chem. 2005 (12), 2352-2359 (2005).
  51. Choudhary, E., Szalai, V. Two-step cycle for producing multiple anodic aluminum oxide (AAO) films with increasing long-range order. RSC Adv. 6 (72), 67992-67996 (2016).
  52. Yuan, J. H., He, F. Y., Sun, D. C., Xia, X. H. A Simple Method for Preparation of Through-Hole Porous Anodic Alumina Membrane. Chem. Mater. 16 (10), 1841-1844 (2004).
  53. Yuan, J. H., Chen, W., Hui, R. J., Hu, Y. L., Xia, X. H. Mechanism of one-step voltage pulse detachment of porous anodic alumina membranes. Electrochim. Acta. 51 (22), 4589-4595 (2006).
  54. Zhao, S., Chan, K., Yelon, A., Veres, T. Preparation of open-through anodized aluminium oxide films with a clean method. Nanotechnology. 18 (24), 245304 (2007).
  55. Brudzisz, A., Brzózka, A., Sulka, G. D. Effect of processing parameters on pore opening and mechanism of voltage pulse detachment of nanoporous anodic alumina. Electrochim. Acta. 178, 374-384 (2015).
  56. Hong, Y. K., Kim, B. H., Kim, D. I., Park, D. H., Joo, J. High-yield and environment-minded fabrication of nanoporous anodic aluminum oxide templates. RSC Adv. 5 (34), 26872-26877 (2015).
  57. Jeong, S. H., et al. Massive, eco-friendly, and facile fabrication of multi-functional anodic aluminum oxides: application to nanoporous templates and sensing platforms. RSC Adv. 7 (8), 4518-4530 (2017).
  58. Houser, J. E., Hebert, K. R. The role of viscous flow of oxide in the growth of self-ordered porous anodic alumina films. Nature Mater. 8 (5), 415-420 (2009).
  59. Jessensky, O., Müller, F., Gösele, U. Self-organized formation of hexagonal pore arrays in anodic alumina. Appl. Phys. Lett. 72 (10), 1173-1175 (1998).
  60. Li, F., Zhang, L., Metzger, R. M. On the Growth of Highly Ordered Pores in Anodized Aluminum Oxide. Chem. Mater. 10 (9), 2470-2480 (1998).
  61. Li, A. P., Müller, F., Bimer, A., Nielsch, K., Gösele, U. Hexagonal pore arrays with a 50-420 nm interpore distance formed by self-organization in anodic alumina. J. Appl. Phys. 84 (11), 6023-6026 (1998).
  62. Nielsch, K., Choi, J., Schwirn, K., Wehrspohn, R. B., Gösele, U. Self-ordering Regimes of Porous Alumina: The 10% Porosity Rule. Nano Lett. 2 (7), 677-680 (2002).
  63. Yanagishita, T., Masuda, H. High-Throughput Fabrication Process for Highly Ordered Through-Hole Porous Alumina Membranes Using Two-Layer Anodization. Electrochim. Acta. 184, 80-85 (2015).

Tags

Anodic Aluminum OxideAAOSimultaneous Multi-surface AnodizationStair-like Reverse BiasesDetachmentSulfuric AcidOxalic AcidElectropolishingAluminum SubstratePerchloric Acid
check_url/it/56432?article_type=t&slug=simultaneous-multi-surface-anodizations-stair-like-reverse-biases

Play Video
PDF
DOI
DOWNLOAD MATERIALS LIST
Citazione di questo articolo
Im, H., Jeong, S. H., Park, D. H., Kim, S., Hong, Y. K. Simultaneous Multi-surface Anodizations and Stair-like Reverse Biases Detachment of Anodic Aluminum Oxides in Sulfuric and Oxalic Acid Electrolyte. J. Vis. Exp. (128), e56432, doi:10.3791/56432 (2017).
Scarica citazione
Ristampe e autorizzazioni

View Video

✖

To prove you're not a robot, please enter the text in the image below

CAPTCHA Image
Play CAPTCHA Audio
Refresh Image