Preparazione di ZnO Nanorod / grafene / ZnO Nanorod epitassiale Doppia Heterostructure per piezoelettrico nanogeneratore utilizzando preriscaldamento Idrotermale
È necessario avere un abbonamento a JoVE per visualizzare questo. Accedi o inizia la tua prova gratuita.
1Department of Nanoenergy Engineering, BK21 Plus Nanoconvergence Technology Division,Pusan National University (PNU), Miryang, 2Department of Cogno-Mechatronics Engineering,Pusan National University (PNU), Busan, 3SKKU Advanced Institute of Nanotechnology (SAINT), Center for Human Interface Nanotechnology (HINT), SKKU-Samsung Graphene Center,Sungkyunkwan University (SKKU)
Capitoli
- 00:05Titolo
- 01:08Chemical Vapor Deposition (CVD) Growth of Single Layered Graphene
- 02:20Preparation of Graphene/Polyethylene Terephthalate (PET) Substrate
- 04:03Synthesis of ZnO Nanorod/Graphene/ZnO Nanorod Epitaxial Double Heterostructure
- 05:23Fabrication of Piezoelectric Nanogenerator
- 07:01Electrical Performance Measurement Setup
- 08:18Results: Scanning Electron Microscopy (SEM) Images of Hydrothermally Grown ZnO Nanorod and Representative Results for the Piezoelectric Nanogenerator
- 10:10Conclusion
Metodo di fabbricazione di uno stadio per l'ottenimento autoportante epitassiale doppio eterostruttura è presentato. Questo approccio potrebbe raggiungere una copertura ZnO con una densità numero maggiore di quella del singolo epitassiale eterostruttura, portando ad un nanogeneratore piezoelettrico con una prestazione elettrica maggiore produzione.