Magnetisches und thermisch empfindliches Poly (<em> N.</em> -isopropylacrylamid) -basierte Mikrogele für die magnetisch getriggerte kontrollierte Freisetzung
É necessária uma assinatura da JoVE para visualizar este conteúdo. Faça login ou comece sua avaliação gratuita.
1Institute of Polymer Science and Engineering,National Taiwan University, 2Department of Materials Engineering,Ming Chi University of Technology, 3Department of Metallurgy and Materials Engineering,Bandung Institute of Technology and Science, 4Department of Chemical Engineering,National Taiwan University, 5Department of Materials Science and Engineering,National Taiwan University
Capítulos
- 00:05Título
- 01:08Synthesis of Organic-inorganic Hybrid Microgels
- 04:15Synthesis and Testing of Curcumin-loaded PNIPAAm/Fe3O4-NH2 Microgels
- 06:25Results: Magnetically-controlled Curcumin Release from Cur-PNIPAAm/Fe3O4-NH2 Microgels
- 08:06Conclusion
Dieses Manuskript beschreibt die Herstellung von magnetischen und wärmeempfindlichen Mikrogelen über eine temperaturinduzierte Emulsion ohne chemische Reaktion. Diese empfindlichen Mikrogele wurden durch Mischen von Poly ( N- isopropylacrylamid) (PNIPAAm), Polyethylenimin (PEI) und Fe 3 O 4 -NH 2 Nanopartikeln für die potentielle Verwendung in magnetisch und thermisch getriggerter Arzneimittelfreisetzung synthetisiert.