定向钢纤维增强水泥基复合材料的制备及其弯曲性能研究

JoVE Journal
Engenharia

É necessária uma assinatura da JoVE para visualizar este conteúdo. Faça login ou comece sua avaliação gratuita.

JoVE Journal Engenharia

Preparation of Aligned Steel Fiber Reinforced Cementitious Composite and Its Flexural Behavior

Please note that all translations are automatically generated. Click here for the English version.

定向钢纤维增强水泥基复合材料的制备及其弯曲性能研究

DOI:

10.3791/56307-v

•

11:07 min

•

June 27, 2018

•

Ru Mu, Luansu Wei, Xiaowei Wang, Hui Li, Longbang Qing, Jian Zhou, Quanming Zhao

¹School of Civil and Transportation Engineering,Hebei University of Technology, ²School of Information Engineering,Hebei University of Technology

Capítulos

00:04Título
00:57Workability Testing
03:17Specimen Preparation
05:36Three-point Bending Test
08:08Results: Flexural Strength Differences between Traditional and Aligned Steel Fiber Reinforced Cementitious Composites
09:39Conclusion

Summary

Tadução automática

本协议描述了一种采用均匀电磁场制造对齐钢纤维增强水泥基复合材料的方法。对钢纤维增强水泥基复合材料具有优异的力学性能。

Tags

Aligned Steel Fiber Cementitious Composite Flexural Behavior Mortar Workability Sinking Depth Mortar Rheometer Superplasticizer Magnetic Field Solenoid Compacting Table

Article

Embed

ADICIONAR À PLAYLIST

Usage Statistics

Vídeos Relacionados

钢管机械性扩张为解决井眼漏

一个测试平台为聚合物的耐久性研究，并在同期Hygrothermo机械刺激纤维增强聚合物复合材料

基于多尺度复合材料的增强与石墨烯纳米片应变传感

不锈钢滑面的制备及高温抗粘接性能研究

提高纤维增强聚合物穗锚质量控制的安装方法

钢筋形态参数评价方法的适用性分析

胶孔溶液的表达及其化学成分和电阻率的 X 射线荧光分析

通过 DP780 钢上的摩擦搅拌点焊生成圈接头

聚酯增强和聚氯乙烯涂层技术织物的人工热老化

石墨烯结构增强的先进自愈合沥青：原子学见解

Read Article