Production of Single Tracks of Ti-6Al-4V by Directed Energy Deposition to Determine the Layer Thickness for Multilayer Deposition

Please note that all translations are automatically generated. Click here for the English version.

多層成膜の層の厚さを決定する指向性エネルギー蒸着法による Ti 6al-4 v の単一トラックの生産

DOI:

10.3791/56966-v

•

09:12 min

•

March 13, 2018

•

Abdollah Saboori, Simona Tusacciu, Mattia Busatto, Manuel Lai, Sara Biamino, Paolo Fino, Mariangela Lombardi

¹Department of Applied Science and Technology,Politecnico di Torino, ²IRIS S.r.l.

Capítulos

00:04Título
01:05Ti-6Al-4V Powder Characterization, Powder Loading, and Sample Preparation
02:36Equipment Preparation and Deposition of Single Tracks
04:50Analysis of Single Tracks
06:22Results: Single Tracks of Ti-6Al-4V
07:58Conclusion

Summary

Tadução automática

本研究では、指向性エネルギー蒸着法による Ti 6al-4 v 材の層の厚さを推定する溶融プールの特性評価に基づく迅速法を開発します。

Tags

Directed Energy Deposition Additive Manufacturing Ti-6Al-4V Layer Thickness Melt Pool Process Parameters Powder Characterization FESEM Apparent Density Chemical Analysis Powder Loading Nozzle Positioning

Article

Embed

ADICIONAR À PLAYLIST

Usage Statistics

Vídeos Relacionados

電荷分離ナノ結晶とその固体の手段によって太陽エネルギーを収穫

パルスレーザー蒸着法によるナノエンジニアリング透明導電性酸化物の作製

気孔率に複製技術とエフェクトでオープンセルアルミフォームの製造のためのプロトコルのキャスト

熱蒸着および原子層堆積法によって記録し、効率のSnS太陽電池を作ります

エアロゾルデポジション法を用いて厚い高密度イットリウム鉄ガーネット膜の形成

プラズマによる高c軸ZnO薄膜の合成とキャラクタリゼーションは、化学気相堆積システムとそのUV光検出器アプリケーションを強化しました

転写印刷により水素化微結晶シリコン太陽電池の光トラッピング銀ナノ構造の統合

均一な厚さのGeのエレクトロスプレーデポジション<sub> 23</sub> Sbの<sub> 7</sub> S<sub> 70</sub>と同様に<sub> 40</sub> S<sub> 60</sub>カルコゲナイドガラスフィルム

によってナノ構造イットリア安定化ジルコニア（YSZ）足場の高温製作<em>その場での</em>カーボンテンプレート化キセロゲル

斜め蒸着を使用してメディアを高吸収極薄カラーフィルムの作製

Read Article