Sintesi di nanocompositi di grafene-idrossiapatite per un potenziale utilizzo nell'ingegneria dei tessuti ossei
É necessária uma assinatura da JoVE para visualizar este conteúdo. Faça login ou comece sua avaliação gratuita.
1Department of Physics, Faculty of Science,Kasetsart University, 2Department of Microbiology, School of Science,RK. University, 3Department of Chemical Engineering,Northeastern University, 4Defence Institute of Advanced Technology Campus,Navyukti Innovations Pvt. Ltd., 5Department of Biomedical Engineering,Hebei University of Technology, 6Department of Chemistry, Saveetha School of Engineering, Institute of Medical and Technical Science,Saveetha University, 7UFPI – Universidade Federal do Piauí
Capítulos
- 00:04Introduction
- 00:49Synthesis of nHAP by Precipitation
- 01:52Preparation of nHAP/GNR Nanocomposites
- 04:17Results: Characterization of Graphene-Hydroxyapatite Nanocomposites
- 06:30Conclusion
Nuovi nanocompositi di nanonastri di grafene e nanoparticelle di idrossiapatite sono stati preparati utilizzando la sintesi in fase di soluzione. Questi ibridi quando impiegati in scaffold bioattivi possono presentare potenziali applicazioni nell'ingegneria tissutale e nella rigenerazione ossea.