Potentiodynamique Testing Corrosion

Published: September 04, 2016
doi:

Summary

Here, we present a protocol to set up and run an in vitro potentiodynamic corrosion system to analyze pitting corrosion for small metallic medical devices.

Abstract

Different metallic materials have different polarization characteristics as dictated by the open circuit potential, breakdown potential, and passivation potential of the material. The detection of these electrochemical parameters identifies the corrosion factors of a material. A reliable and well-functioning corrosion system is required to achieve this.

Corrosion of the samples was achieved via a potentiodynamic polarization technique employing a three-electrode configuration, consisting of reference, counter, and working electrodes. Prior to commencement a baseline potential is obtained. Following the stabilization of the corrosion potential (Ecorr), the applied potential is ramped at a slow rate in the positive direction relative to the reference electrode. The working electrode was a stainless steel screw. The reference electrode was a standard Ag/AgCl. The counter electrode used was a platinum mesh. Having a reliable and well-functioning in vitro corrosion system to test biomaterials provides an in-expensive technique that allows for the systematic characterization of the material by determining the breakdown potential, to further understand the material’s response to corrosion. The goal of the protocol is to set up and run an in vitro potentiodynamic corrosion system to analyze pitting corrosion for small metallic medical devices.

Introduction

techniques électrochimiques fournissent une méthode rapide et relativement peu coûteux pour obtenir les propriétés électrochimiques d'un matériau. Ces techniques reposent principalement sur ​​la capacité de détecter la corrosion d'un métal en observant la réaction du processus de transfert de charge à une perturbation électrochimique contrôlée 1-5. La corrosion des implants métalliques dans un environnement de corps est critique en raison des conséquences néfastes sur la biocompatibilité et de matériel d' intégrité 6. Le principal facteur contribuant à la corrosion des implants à l' intérieur du corps est la dissolution de l'oxyde de surface conduisant à une libération accrue d'ions métalliques 7-11. Cela se traduit par des réactions biologiques indésirables, qui peut être trouvé localement, mais avec des effets potentiellement systémique conduisant à une défaillance prématurée de l'implant 10,12-28.

Les caractéristiques de la corrosion d'un échantillon d'essai sont prédites à partir de l'analyse de polarisation produitepar un potentiostat. Une analyse de polarisation permet l'extrapolation des paramètres cinétiques et la corrosion d'un substrat métallique. Lors d'un balayage, l'oxydation ou la réduction d'une espèce électro-active sont limitées par le transfert de charge et le mouvement des corps réactionnels ou des produits. Tous ces facteurs sont encapsulés par le balayage de polarisation; donc l'importance d'avoir un système qui produit une analyse de polarisation fiable et reproductible sur plusieurs cycles est d'une grande importance. L'objectif principal de ce manuscrit est de fournir un protocole d'identifier les raisons et les mesures prises pour obtenir un système de corrosion potentiodynamique fonctionne bien.

Protocol

1. Construction du titulaire échantillon Construire le porte-échantillon à partir des entretoises en acier inoxydable et une vis en acier inoxydable M3 filetée, tenue en place avec un écrou hexagonal M3. Retirez la tête de la vis filetée avec une pince et polir le segment de coupe pour maintenir le modèle de fil. Lorsque tous les composants individuels sont prêts, assembler les porte-électrodes. Chaque porte-électrode contient trois entretoises réunies par les vis M3 résultant…

Representative Results

A l'issue de la procédure un système in vitro de la corrosion dans l' installation est de mener des études de corrosion. Des procédures spécifiques tels que le nettoyage de la cuve de la corrosion et la cage de Faraday ont été introduits dans le protocole pour améliorer les performances de bruit. Le concept fondamental d'une bonne analyse de polarisation est d'identifier les conditions électro-physiques du matériau fournissant des informations …

Discussion

Les analyses de polarisation obtenus à partir des échantillons d'acier inoxydable ont montré des parcelles continues propres corrélant avec des scans vus dans la littérature indicative d'un système qui fonctionne bien à la corrosion , qui est à la fois fiable et reproductible 29. Une mauvaise reproductibilité des potentiels de piqûres potentiodynamiques est identifié avec un écart de quelques centaines de millivolts, avec piqûres potentiel étant caractérisé par un processus stochastiqu…

Disclosures

The authors have nothing to disclose.

Acknowledgements

The authors had no funding provided for this study.

Materials

Potentiostat Metrohm PGSTAT101
Ag/AgCl reference electrode, shielded Metrohm 6.0729.100
Electrode shaft Metrohm 6.1241.060
Polisher Forcipol 1v Metkon 3602
Clindrical flask 700mL SciLabware FR700F
Reaction lid SciLabware MAF2/41
Dichloromethane Sigma-Aldrich MKBR7629V use under a fumehood. Wear protective clothing
Thermo / HAAKE D Series Immersion Circulators Haake

References

  1. Isaacs, H. S. Aspects of corrosion from the ECS Publications. J. Electrochem. Soc. 149 (12), 85-87 (2002).
  2. Fontana, M. G., Greene, N. D. . Corrosion Engineering. , (1978).
  3. Pourbaix, M. Electrochemical corrosion of metallic biomaterials. Biomaterials. 5 (3), 122-134 (1984).
  4. Rechnitz, G. A. . Controlled-Potential Analysis. , (1963).
  5. Silverman, D. C., Revie, R. W. Chapter 68. Uhlig’s Corrosion Handbook. , (2000).
  6. Gurappa, I. Characterization of different materials for corrosion resistance under simulated body fluid conditions. Mater Charact. 49 (1), 73-79 (2002).
  7. Antoniou, J., et al. Metal ion levels in the blood of patients after hip resurfacing: a comparison between twenty-eight and thirty-six-millimeter-head metal-on-metal prostheses. J Bone Joint Surg Am. 90, 142-148 (2008).
  8. Billi, F., Campbell, P. Nanotoxicology of metal wear particles in total joint arthroplasty: a review of current concepts. J Appl Biomater Funct Mater. 8 (1), 1-6 (2010).
  9. Bradberry, S. M., Wilkinson, J. M., Ferner, R. E. Systemic toxicity related to metal hip prostheses. Clin Toxicol (Phila). 52 (8), 837-847 (2014).
  10. Davda, K., Lali, F. V., Sampson, B., Skinner, J. A., Hart, A. J. An analysis of metal ion levels in the joint fluid of symptomatic patients with metal-on-metal hip replacements. J Bone Joint Surg Br. 93 (6), 738-745 (2011).
  11. Clarke, M. T., Lee, P. T., Arora, A., Villar, R. N. Levels of metal ions after small and large diameter metal-on-metal hip arthroplasty. J Bone Joint Surg Br. 85 (6), 913-917 (2003).
  12. Brown, S. A., Hughes, P. J., Merritt, K. In vitro studies of fretting corrosion of orthopaedic materials. J Orthop Res. 6 (4), 572-579 (1988).
  13. Bryant, M., et al. Characterisation of the surface topography, tomography and chemistry of fretting corrosion product found on retrieved polished femoral stems. J Mech Behav Biomed Mater. 32, 321-334 (2014).
  14. Jantzen, C., Jørgensen, H. L., Duus, B. R., Sporring, S. L., Lauritzen, J. B. Chromium and cobalt ion concentrations in blood and serum following various types of metal-on-metal hip arthroplasties. A literature review. Acta Orthopaedica. 84 (3), 229-236 (2013).
  15. Campbell, P., et al. Histological Features of Pseudotumor-like Tissues From Metal-on-Metal Hips. Clin. Orthop. Relat. Res. 468 (9), 2321-2327 (2010).
  16. Cook, S. D., et al. The in vivo performance of 250 internal fixation devices: a follow-up study. Biomaterials. 8 (3), 177-184 (1987).
  17. Cooper, H. J., Urban, R. M., Wixson, R. L., Meneghini, R. M., Jacobs, J. J. Adverse local tissue reaction arising from corrosion at the femoral neck-body junction in a dual-taper stem with a cobalt-chromium modular neck. J Bone Joint Surg Am. 95 (10), 865-872 (2013).
  18. Langton, D. J., Sprowson, A. P., Joyce, T. J., Reed, M., Carluke, I., Partington, P., Nargol, A. V. Blood metal ion concentrations after hip resurfacing arthroplasty. J Bone Joint Surg Br. 91 (10), 1287-1295 (2009).
  19. Langton, D. J., Jameson, S. S., Joyce, T. J., Webb, J., Nargol, A. V. The effect of component size and orientation on the concentrations of metal ions after resurfacing arthroplasty of the hip. J Bone Joint Surg Br. 90 (9), 1143-1151 (2008).
  20. Daniel, J., Ziaee, H., Pradhan, C., McMinn, D. J. Six-year results of a prospective study of metal ion levels in young patients with metal-on-metal hip resurfacings. J Bone Joint Surg Br. 91 (2), 176-179 (2009).
  21. De Haan, R., et al. Correlation between inclination of the acetabular component and metal ion levels in metal-on-metal hip resurfacing replacement. J Bone Joint Surg Br. 90 (10), 1291-1297 (2008).
  22. Dijkman, M. A., de Vries, I., Mulder-Spijkerboer, H., Meulenbelt, J. Cobalt poisoning due to metal-on-metal hip implants. Ned Tijdschr Geneeskd. 156 (42), A4983 (2012).
  23. Fisher, J. Bioengineering reasons for the failure of metal-on-metal hip prostheses: an engineer’s perspective. J Bone Joint Surg Br. 93 (8), 1001-1004 (2011).
  24. Goldberg, J. R., et al. A Multicenter Retrieval Study of the Taper Interfaces of Modular Hip Prostheses. Clin. Orthop. Relat. Res. (401), 149-161 (2002).
  25. Ingham, E., Fisher, J. Biological reactions to wear debris in total joint replacement. Proc Inst Mech Eng H. 214 (1), 21-37 (2000).
  26. Gilbert, J. L., Buckley, C. A., Jacobs, J. J., Res, J. .. B. i. o. m. e. d. .. M. a. t. e. r. .. In vivo corrosion of modular hip prosthesis components in mixed and similar metal combinations. The effect of crevice, stress, motion and allot coupling. J. Biomed. Mater. Res. 76 (1), 1533-1544 (1993).
  27. Browne, J. A., Bechtold, C. D., Berry, D. J., Hanssen, A. D., Lewallen, D. G. Failed metal-on-metal hip arthroplasties: a spectrum of clinical presentations and operative findings. Clin. Orthop. Relat. Res. 468 (9), 2313-2320 (2010).
  28. Jantzen, C., Jorgensen, H. L., Duus, B. R., Sporring, S. L., Lauritzen, J. B. Chromium and cobalt ion concentrations in blood and serum following various types of metal-on-metal hip arthroplasties: a literature overview. Acta Orthop. 84 (3), 229-236 (2013).
  29. Frangini, S., De Cristofaro, N. Analysis of galvanostatic polarisation method for determining reliable pitting potentials on stainless steels in crevice-free conditions. Corros Sci. 45 (12), 2769-2786 (2002).

Play Video

Cite This Article
Munir, S., Pelletier, M. H., Walsh, W. R. Potentiodynamic Corrosion Testing. J. Vis. Exp. (115), e54351, doi:10.3791/54351 (2016).

View Video