An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature

Please note that all translations are automatically generated. Click here for the English version.

新しいキャスト MnCuNiFeZnAl 合金の優れた能力と高いサービス温度の減衰の準備のための利用可能な手法

DOI:

10.3791/57180-v

•

14:51 min

•

September 23, 2018

•

Dong Li³, Wenbo Liu², Ning Li, Zhenyu Zhong, Jiazhen Yan, Sanqiang Shi

¹School of Manufacturing Science and Engineering,Sichuan University, ²Department of Mechanical Engineering,Hong Kong Polytechnic University, ³Department of Mechanical and Electrical Engineering,Chengdu Aeronautic Polytechnic

Capítulos

00:00Título
01:31Introduction
05:01The Protocol for Alloy Preparation and Test
10:32Representative Results
13:47Conclusion

Summary

Tadução automática

ここで小説の質の高い製錬技術と合理的な熱処理法による優れた包括的なパフォーマンスに Mn-Cu 系合金を取得するためのプロトコルを提案する.

Tags

Cast MnCuNiFeZnAl Alloy Damping Capacity High Service Temperature Vacuum Induction Melting Sand Mold Casting Heat Treatment Microstructure Manganese-copper Based Alloys Face-centered Cubic To Face-centered Tetragonal Phase Transformation Aging Treatment Nanoscale Precipitates

Article

Embed

ADICIONAR À PLAYLIST

Usage Statistics

Vídeos Relacionados

エクストリーム圧力と温度での合成とMicrodiffraction

半導体技術との互換性低温カーボンナノチューブ垂直相互接続の作製

高分解能温度フィールドマッピングのための光ファイバの分散センサ

高温プラズマ診断として使用するためのX線イメージングクリスタル分光法を適用します

ゼオライトH-ZSM-5で高温・高圧のガス吸着用のLangatateクリスタルマイクロバランスに基づいて吸着装置

イオン液体系電解質、リチウムイオン電池の組立、および高温でのパフォーマンスの測定の合成

キャストアルミ部品の暖かいスピニングのための実験手順

によってナノ構造イットリア安定化ジルコニア（YSZ）足場の高温製作<em>その場での</em>カーボンテンプレート化キセロゲル

ステンレス鋼の滑りやすい表面の作製と高温の反付着挙動

磁石は、複合材生産を支援: 柔軟な新しい技術高圧真空袋/Lay アッププロセスを達成するため

Read Article