Cutting Procedures, Tensile Testing, and Ageing of Flexible Unidirectional Composite Laminates

Please note that all translations are automatically generated. Click here for the English version.

柔軟な単方向複合ラミネートの切断手順、引張試験、およびエージング

DOI:

10.3791/58991-v

•

07:53 min

•

April 27, 2019

•

Amy Engelbrecht-Wiggans², Ajay Krishnamurthy², Faraz Burni³, William Osborn, Amanda L. Forster

¹Material Measurement Laboratory,National Institute of Standards and Technology, ²Theiss Research, ³Chemical and Biomolecular Engineering Department,University of Maryland

Capítulos

00:04Título
00:38Cutting Procedure for Warp-direction Specimens, Cut Perpendicular to Roll Axis
03:00Tensile Testing of Unidirectional Laminate Specimens
04:36Beginning an Aging Experiment
05:23Extracting Aged Material Strips for Analysis
06:33Results: Load versus Extension Plots and Failure Stress Distributions
07:27Conclusion

Summary

Tadução automática

本研究の目的は、高強度アラミドまたは超高モル質量ポリエチレンベースの柔軟な単方向複合ラミネート材料の正確な機械的試験のための一貫した標本を準備するためのプロトコルを開発し、記述することであったこれらの材料の人工老化を行うためのプロトコル。

Tags

Keywords: Unidirectional Composite Flexible Composite Tensile Testing Cutting Procedure Ageing Fiber Direction Specimen Preparation Soft Body Armor

Article

Embed

ADICIONAR À PLAYLIST

Usage Statistics

Vídeos Relacionados

シングルラップせん断試験を経て溶接継手の機械的特性評価のための熱可塑性コンポジットクーポンの超音波溶接

商工会議システムを用いたナノ材料を含む複合からのナノ粒子のリリースのテスト

単方向生地のためのテストをウィッキング：キャピラリーパラメータの測定を液体複合成形プロセスに毛細管圧力を評価します

磁石は、複合材生産を支援: 柔軟な新しい技術高圧真空袋/Lay アッププロセスを達成するため

ポリエステル強化およびポリ塩化ビニルコーティング技術織物の人工熱老化

直交重ね合わせレオロジーの校正手順

顕微鏡搭載Y字型切削試験の実施

異なる製造プロセスで得られたガラス繊維強化ポリマー複合積層物の機械的特性の測定

超高感度検出のためのポリジメチルシロキサン(PDMS)ベースのフレキシブル表面増強ラマン散乱(SERS)基板の作製

ウェットハンドレイアップ/真空バッグ(WLVB)法によるガラス繊維強化ポリマー(GFRP)複合積層板の作製

Read Article