Summary

In Situ Síntesis de nanopartículas de oro sin agregación en el espacio entre capas de Capas de titanato películas transparentes

Published: January 17, 2017
doi:

Summary

A continuación, se presenta un protocolo para la síntesis in situ de nanopartículas de oro (AuNPs) dentro del espacio de capa intermedia de películas titanato estratificado sin la agregación de AuNPs. No se observó cambio espectral incluso después de 4 meses. El material sintetizado se espera que las aplicaciones en catálisis, fotocatálisis, y el desarrollo de dispositivos plasmónicas rentables.

Abstract

Combinations of metal oxide semiconductors and gold nanoparticles (AuNPs) have been investigated as new types of materials. The in situ synthesis of AuNPs within the interlayer space of semiconducting layered titania nanosheet (TNS) films was investigated here. Two types of intermediate films (i.e., TNS films containing methyl viologen (TNS/MV2+) and 2-ammoniumethanethiol (TNS/2-AET+)) were prepared. The two intermediate films were soaked in an aqueous tetrachloroauric(III) acid (HAuCl4) solution, whereby considerable amounts of Au(III) species were accommodated within the interlayer spaces of the TNS films. The two types of obtained films were then soaked in an aqueous sodium tetrahydroborate (NaBH4) solution, whereupon the color of the films immediately changed from colorless to purple, suggesting the formation of AuNPs within the TNS interlayer. When only TNS/MV2+ was used as the intermediate film, the color of the film gradually changed from metallic purple to dusty purple within 30 min, suggesting that aggregation of AuNPs had occurred. In contrast, this color change was suppressed by using the TNS/2-AET+ intermediate film, and the AuNPs were stabilized for over 4 months, as evidenced by the characteristic extinction (absorption and scattering) band from the AuNPs.

Introduction

Varios nanopartículas de metales nobles (MNPS) presentan colores o tonos característicos debido a su resonancia de plasmones superficiales (localizada) LSPR propiedades; Por lo tanto, MNPs pueden ser utilizados en diversas aplicaciones / fotoquímicos ópticos y o 1-4. Recientemente, combinaciones de semiconductor de óxido metálico (MOS) fotocatalizadores, tales como óxido de titanio (TiO 2) y MNPs, se han investigado a fondo como nuevos tipos de fotocatalizadores 5-14. Sin embargo, en muchos casos, cantidades muy pequeñas de MNPs existir en la superficie MOS, porque la mayoría de las partículas de MOS tienen áreas superficiales relativamente bajas. Por otro lado, en capas de semiconductores de óxido de metal (LMOSs) exhiben propiedades fotocatalíticas y tienen un área superficial grande, típicamente de varios cientos de metros cuadrados por unidad g de un OVM 15-17. Además, varios LMOSs tienen propiedades de intercalación (es decir, varias especies químicas se pueden acomodar dentro de sus espacios entre capas expandibles y grandes) 15-20. Por lo tanto, con una combinación de MNPs y LMOSs, se espera que cantidades relativamente grandes de MNPs se hibridan con los fotocatalizadores semiconductores.

Nos han informado de la primera síntesis in situ de nanopartículas de cobre (21) CuNPs dentro del espacio de capa intermedia de OVM (óxido de titanio nanosheet; TNS 16-30) películas transparentes a través de pasos muy sencillos. Sin embargo, aún no se ha informado de los detalles de los procedimientos de síntesis y la caracterización de los otros híbridos MNPs y TNS nobles. Por otra parte, los CuNPs dentro de las capas de TNS se oxidaron fácilmente y se decolora en condiciones ambientales 21. Como tal, nos centramos en las nanopartículas de oro (AuNPs), porque AuNPs son ampliamente utilizados para diversos óptica, fotoquímico, y aplicaciones catalíticas, y se espera que sean relativamente estable frente a la oxidación 3-5,7,8,10-14 , 28,31,32. Aquí, se presenta la síntesis de AuNPs dentro del espacio de capa intermedia de TNS y mostrar tha2 t-ammoniumethanethiol (2-AET +; Figura 1 recuadro) funciona efectivamente como un reactivo de protección para AuNPs dentro de la capa intermedia de TNS.

Protocol

Precaución: Siempre tenga cuidado cuando se trabaja con productos químicos y soluciones. Siga las prácticas de seguridad apropiadas y usar guantes, gafas y una bata de laboratorio en todo momento. Tenga en cuenta que los nanomateriales pueden tener riesgos adicionales en comparación con su contraparte mayor. 1. Preparación de Regentes Preparar la solución de metil viológeno acuosa mediante la disolución de 0,0012 g de dicloruro de 1,1'-dimetil-4,4'-bipiridinio (metil viológeno; MV <su…

Representative Results

Se utilizaron dos tipos de películas precursoras en este estudio (es decir, con y sin el reactivo de protección (2-AET +) dentro de la capa intermedia de TNS). En ausencia de 2-AET +, 1,1'-bipiridinio-dimetil-4,4' dicloruro de (viológeno de metilo; MV 2 +) se usó como un expansor del espacio entre capas, porque MV 2 + que contienen LMOSs haber sido se utiliza con frecuencia como intermedios en el método de intercambio de i…

Discussion

Este manuscrito proporciona un protocolo detallado para la síntesis in situ de nanopartículas de oro (AuNPs) dentro del espacio entre capas de las películas de TNS. Este es el primer informe de la síntesis in situ de AuNPs dentro del espacio entre capas de TNS. Por otra parte, se encontró que la 2-AET + funciona como un reactivo de protección eficaz para AuNPs dentro de la capa intermedia de TNS. Estos métodos se hibridan AuNPs y TNS películas transparentes. TNS películas con buena …

Disclosures

The authors have nothing to disclose.

Acknowledgements

This work was partly supported by Nippon Sheet Glass Foundation for Materials Science and Engineering and JSPS KAKENHI (Grant-in-Aid for Challenging Exploratory Research, #50362281).

Materials

Methyl viologen dichloride Aldrich Chemical  Co., Inc. 1910-42-5
Tetrabutylammonium hydroxide TCI T1685
cesium carbonate Kanto Chemical Co., Inc. 07184-33
anatase titanium dixoide Ishihara Sangyo Ltd. ST-01
hydrochloric acid Junsei Chemical Co., Ltd. 20010-0350
sodium hydroxide Junsei Chemical Co., Ltd. 195-13775
Tetrachloroauric(III) acid trihydrate Kanto Chemical Co., Inc. 17044-60
sodium tetrahydroborate Junsei Chemical Co., Ltd. 39245-1210
2-ammoniumethanethiol hydrochloride TCI A0296
Ultrapure water (0.056 µS/cm) Milli-Q water purification system (Direct-Q® 3UV, Millipore)
Microscope slide (Thickness : 1.0∼1.2 mm) Matsunami glass Co., Ltd.

References

  1. Kelly, K. L., Coronado, E., Zhao, L. L., Schatz, G. C. The Optical Properties of Metal Nanoparticles: The Influence of Size, Shape, and Dielectric Environment. J. Phys. Chem. B. 107 (3), 668-677 (2003).
  2. Rycenga, M., et al. Controlling the Synthesis and Assembly of Silver Nanostructures for Plasmonic Applications. Chem. Rev. 111 (6), 3669-3712 (2011).
  3. The Binh, N., et al. Preparation of metal nanoparticles for surface enhanced Raman scattering by laser ablation method. Adv. Nat. Sci.: Nanosci. Nanotechnol. 3 (2), 025016 (2012).
  4. Chen, H., Shao, L., Li, Q., Wang, J. Gold nanorods and their plasmonic properties. Chem. Soc. Rev. 42 (7), 2679-2724 (2013).
  5. Subramanian, V., Wolf, E. E., Kamat, P. V. Influence of Metal/Metal Ion Concentration on the Photocatalytic Activity of TiO2-Au Composite Nanoparticles. Langmuir. 19 (2), 469-474 (2003).
  6. Linic, S., Christopher, P., Ingram, D. B. Plasmonic-metal nanostructures for efficient conversion of solar to chemical energy. Nat Mater. 10 (12), 911-921 (2011).
  7. Gomes Silva, C., Juárez, R., Marino, T., Molinari, R., García, H. Influence of Excitation Wavelength (UV or Visible Light) on the Photocatalytic Activity of Titania Containing Gold Nanoparticles for the Generation of Hydrogen or Oxygen from Water. J. Am. Chem. Soc. 133 (3), 595-602 (2011).
  8. Hou, W., et al. Photocatalytic Conversion of CO2 to Hydrocarbon Fuels via Plasmon-Enhanced Absorption and Metallic Interband Transitions. ACS Catal. 1 (8), 929-936 (2011).
  9. Wang, W. -. N., et al. Size and Structure Matter: Enhanced CO2 Photoreduction Efficiency by Size-Resolved Ultrafine Pt Nanoparticles on TiO2 Single Crystals. J. Am. Chem. Soc. 134 (27), 11276-11281 (2012).
  10. Shi, X., Ueno, K., Takabayashi, N., Misawa, H. Plasmon-Enhanced Photocurrent Generation and Water Oxidation with a Gold Nanoisland-Loaded Titanium Dioxide Photoelectrode. J. Phys. Chem. C. 117 (6), 2494-2499 (2013).
  11. Tanaka, A., Sakaguchi, S., Hashimoto, K., Kominami, H. Preparation of Au/TiO2 with Metal Cocatalysts Exhibiting Strong Surface Plasmon Resonance Effective for Photoinduced Hydrogen Formation under Irradiation of Visible Light. ACS Catal. 3 (1), 79-85 (2013).
  12. Bian, Z., Tachikawa, T., Zhang, P., Fujitsuka, M., Majima, T. Au/TiO2 Superstructure-Based Plasmonic Photocatalysts Exhibiting Efficient Charge Separation and Unprecedented Activity. J. Am. Chem. Soc. 136 (1), 458-465 (2014).
  13. Ide, Y., et al. Hybridization of Au nanoparticle-loaded TiO2 with BN nanosheets for efficient solar-driven photocatalysis. J. Mater. Chem. A. 2 (12), 4150-4156 (2014).
  14. Zheng, Z., Tachikawa, T., Majima, T. Plasmon-induced spatial electron transfer between single Au nanorods and ALD-coated TiO2: dependence on TiO2 thickness. Chem. Commun. 51 (76), 14373-14376 (2015).
  15. Inui, Y., et al. Reversible redox processes of poly(anilines) in layered semiconductor niobate films under alternate UV-Vis light illumination. J. Phys. Chem. B. 111 (42), 12162-12169 (2007).
  16. Yui, T., Takagi, K., Ariga, K., Nalwa, H. S. . Bottom-up Nanofabrication Vol. 5. 5, 35-90 (2009).
  17. Sasai, R., Yui, T., Takagi, K., Nalwa, H. S. . Encyclopedia of Nanoscience and Nanotechnology Vol. 24. , 303-361 (2011).
  18. Yui, T., et al. Visible light-induced electron transfers in titania nanosheet and mesoporous silica integrated films. Bull. Chem. Soc. Jpn. 79 (3), 386-396 (2006).
  19. Yui, T., et al. Photoinduced one-electron reduction of MV2+ in titania nanosheets using porphyrin in mesoporous silica thin films. Langmuir. 21 (7), 2644-2646 (2005).
  20. Yui, T., et al. Remarkably stabilized charge separations in inorganic nanospace. Bull. Chem. Soc. Jpn. 82 (7), 914-916 (2009).
  21. Sasaki, K., et al. Synthesis of copper nanoparticles within the interlayer space of titania nanosheet transparent films. J. Mater. Chem. C. 4 (7), 1476-1481 (2016).
  22. Sasaki, T., Komatsu, Y., Fujiki, Y. A new layered hydrous titanium dioxide HTi2 -/4O4[middle dot]H2O. J. Chem. Soc., Chem. Commun. (12), 817-818 (1991).
  23. Sasaki, T., Watanabe, M. Osmotic Swelling to Exfoliation. Exceptionally High Degrees of Hydration of a Layered Titanate. J. Am. Chem. Soc. 120 (19), 4682-4689 (1998).
  24. Yui, T., et al. Synthesis of photofunctional titania nanosheets by electrophoretic deposition. Chem. Mater. 17 (1), 206-211 (2005).
  25. Tachikawa, T., Yui, T., Fujitsuka, M., Takagi, K., Majima, T. Photocatalytic electron transfer in hybrid titania nanosheets studied by nanosecond laser flash photolysis. Chem. Lett. 34 (11), 1522-1523 (2005).
  26. Zhou, Y., Ma, R., Ebina, Y., Takada, K., Sasaki, T. Multilayer Hybrid Films of Titania Semiconductor Nanosheet and Silver Metal Fabricated via Layer-by-Layer Self-Assembly and Subsequent UV Irradiation. Chem. Mater. 18 (5), 1235-1239 (2006).
  27. Yui, T., et al. Photochemical electron transfer though the interface of hybrid films of titania nano-sheets and mono-dispersed spherical mesoporous silica particles. Phys. Chem. Chem. Phys. 8 (39), 4585-4590 (2006).
  28. Sakai, N., Sasaki, T., Matsubara, K., Tatsuma, T. Layer-by-layer assembly of gold nanoparticles with titania nanosheets: control of plasmon resonance and photovoltaic properties. J. Mater. Chem. 20 (21), 4371-4378 (2010).
  29. Yui, T., et al. Photoinduced Electron Transfer between the Anionic Porphyrins and Viologens in Titania Nanosheets and Monodisperse Mesoporous Silica Hybrid Films. ACS Appl. Mater. Interfaces. 3 (4), 931-935 (2011).
  30. Wang, L., Sasaki, T. Titanium Oxide Nanosheets: Graphene Analogues with Versatile Functionalities. Chem. Rev. 114 (19), 9455-9486 (2014).
  31. Eguchi, M., Ito, M., Ishibashi, T. -. a. Stabilization and Modification of Gold Nanocube Surfaces with Layered Silicate. Chem. Lett. 43 (1), 140-142 (2014).
  32. Fujimura, T., Yoshida, Y., Inoue, H., Shimada, T., Takagi, S. Dense Deposition of Gold Nanoclusters Utilizing a Porphyrin/Inorganic Layered Material Complex as the Template. Langmuir. 31 (33), 9142-9147 (2015).
  33. Tong, Z., Shichi, T., Takagi, K. Visible-Light Induced Charge-Separation between Consecutively Cast Porphyrin and Methyl Viologen Multilayered Titanoniobate Hybrid Films. J. Phys. Chem. B. 106 (51), 13306-13310 (2002).
  34. Tong, Z., Shichi, T., Oshika, K., Takagi, K. A Nanostructured Hybrid Material Synthesized by the Intercalation of Porphyrin into Layered Titanoniobate. Chem. Lett. 31 (9), 876-877 (2002).
  35. Tong, Z., Takagi, S., Tachibana, H., Takagi, K., Inoue, H. Novel Soft Chemical Method for Optically Transparent Ru(bpy)3-K4Nb6O17 Thin Film. J. Phys. Chem. B. 109 (46), 21612-21617 (2005).
  36. Hattori, T., et al. Hybridization of layered niobates with cationic dyes. Res. Chem. Intermed. 32 (7), 653-669 (2006).
  37. Moreau, F., Bond, G. C., Taylor, A. O. Gold on titania catalysts for the oxidation of carbon monoxide: control of pH during preparation with various gold contents. J. Catal. 231 (1), 105-114 (2005).
  38. Ivanova, S., Petit, C., Pitchon, V. A new preparation method for the formation of gold nanoparticles on an oxide support. Appl. Cat. A. 267 (1-2), 191-201 (2004).
  39. Sasaki, T., Watanabe, M., Hashizume, H., Yamada, H., Nakazawa, H. Macromolecule-like Aspects for a Colloidal Suspension of an Exfoliated Titanate. Pairwise Association of Nanosheets and Dynamic Reassembling Process Initiated from It. J. Am. Chem. Soc. 118 (35), 8329-8335 (1996).
  40. Tanaka, T., Ebina, Y., Takada, K., Kurashima, K., Sasaki, T. Oversized Titania Nanosheet Crystallites Derived from Flux-Grown Layered Titanate Single Crystals. Chem. Mater. 15 (18), 3564-3568 (2003).
  41. . . Denkikagaku Binran, 5th edn. , (2000).
  42. Shannon, R. D. Revised effective ionic radii and systematic studies of interatomic distances in halides and chalcogenides. Acta Cryst. 32, 751-767 (1976).
  43. Jia, Y. Q. Crystal radii and effective ionic radii of the rare earth ions. J. Solid State Chem. 95 (1), 184-187 (1991).
  44. Grabar, K. C., Freeman, R. G., Hommer, M. B., Natan, M. J. Preparation and Characterization of Au Colloid Monolayers. Anal. Chem. 67 (4), 735-743 (1995).
  45. Niidome, T., Nakashima, K., Takahashi, H., Niidome, Y. Preparation of primary amine-modified gold nanoparticles and their transfection ability into cultivated cells. Chem. Commun. (17), 1978-1979 (2004).
  46. Kawano, T., Horiguchi, Y., Niidome, Y., Niidome, T., Yamada, S. Preparation of Cationic Gold Nanoparticle in Aqueous Solutions of 2-Aminoethanethiol Hydrochloride. Bunseki Kagaku. 54 (6), 521-526 (2005).
  47. Tong, Z., Shichi, T., Kasuga, Y., Takagi, K. The Synthesis of Two Types of Layered Niobate Hybrid Materials by the Selective Intercalation of Ionic Porphyrin. Chem. Lett. 31 (12), 1206-1207 (2002).
  48. Zhao, S., Chen, S., Wang, S., Quan, Z. Composite Au/TiO2 Nanoparticles: Synthesis, Characterization, and Assembly by Using Potentiostatic Technique. J. Colloid Interface Sci. 221 (2), 161-165 (2000).
  49. Negishi, Y., Nobusada, K., Tsukuda, T. Glutathione-Protected Gold Clusters Revisited: Bridging the Gap between Gold(I)-Thiolate Complexes and Thiolate-Protected Gold Nanocrystals. J. Am. Chem. Soc. 127 (14), 5261-5270 (2005).
  50. Schmidt-Stein, F., et al. X-ray induced photocatalysis on TiO2 and TiO2 nanotubes: Degradation of organics and drug release. Electrochem. Commun. 11 (11), 2077-2080 (2009).
  51. Tamura, K., et al. X-ray induced photoelectrochemistry on TiO2. Electrochim. Acta. 52 (24), 6938-6942 (2007).

Play Video

Cite This Article
Sasaki, K., Matsubara, K., Kawamura, S., Saito, K., Yagi, M., Yui, T. In Situ Synthesis of Gold Nanoparticles without Aggregation in the Interlayer Space of Layered Titanate Transparent Films. J. Vis. Exp. (119), e55169, doi:10.3791/55169 (2017).

View Video