Herstellung von ZnO-Nanostäbchen / Graphene / ZnO-Nanostäbchen Epitaxial Doppelheterostruktur für Piezoelektrische Nanogenerator mithilfe Vorwärmen Hydrothermale
A subscription to JoVE is required to view this content. Sign in or start your free trial.
1Department of Nanoenergy Engineering, BK21 Plus Nanoconvergence Technology Division,Pusan National University (PNU), Miryang, 2Department of Cogno-Mechatronics Engineering,Pusan National University (PNU), Busan, 3SKKU Advanced Institute of Nanotechnology (SAINT), Center for Human Interface Nanotechnology (HINT), SKKU-Samsung Graphene Center,Sungkyunkwan University (SKKU)
Chapters
- 00:05Title
- 01:08Chemical Vapor Deposition (CVD) Growth of Single Layered Graphene
- 02:20Preparation of Graphene/Polyethylene Terephthalate (PET) Substrate
- 04:03Synthesis of ZnO Nanorod/Graphene/ZnO Nanorod Epitaxial Double Heterostructure
- 05:23Fabrication of Piezoelectric Nanogenerator
- 07:01Electrical Performance Measurement Setup
- 08:18Results: Scanning Electron Microscopy (SEM) Images of Hydrothermally Grown ZnO Nanorod and Representative Results for the Piezoelectric Nanogenerator
- 10:10Conclusion
Ein-Schritt-Herstellungsverfahren für den Erhalt von freistehenden epitaktischen Doppelheterostruktur dargestellt. Dieser Ansatz könnte ZnO Abdeckung mit einer höheren Dichte als die Anzahl der epitaxialen Einzelheterostruktur zu erzielen, die zu einem piezoelektrischen Nanogenerator mit einem erhöhten elektrischen Ausgangsleistung.