Monolithes de Microhoneycomb préparés par la lyophilisation unidirectionnel de nanofibres Cellulose basé Sols : méthode et Extensions
A subscription to JoVE is required to view this content. Sign in or start your free trial.
1Engineering Laboratory for Functionalized Carbon Materials and Shenzhen Key Laboratory for Graphene-based Materials, Graduate School at Shenzhen,Tsinghua University, 2School of Materials Science and Engineering,Tsinghua University, 3Institute of Multidisciplinary Research for Advanced Materials,Tohoku University, 4Tsinghua-Berkeley Shenzhen Institute (TBSI),Tsinghua University, 5School of Chemical Engineering and Technology,Tianjin University
Chapters
- 00:04Title
- 00:57Preparation of 1 wt% (2,2,6,6-Tetramethylpiperidin-1-yl) oxyl (TEMPO)-mediated Oxidized Cellulose Nanofiber (TOCN) Sol
- 04:01Preparation of TOCN-TiO2 and TOCN-surface-oxidized Carbon Fiber (SOCF) Mixed Sols
- 04:59Microhoneycomb Monolith (MHM) Preparation from 1 Wt% TOCN Sol (MHM-TOCN) or TOCN Mixed Sols (MHM-TOCN/SBR, MHM-TOCN/TiO2, MHM-TOCN/SOCF)
- 06:54Results: Morphologies of the MHM-TOCN, MHM-TOCN/SBR, MHM-TOCN/TiO2, and MHM-TOCN/SOCF
- 08:39Conclusion
Nous présentons ici un protocole général pour préparer une variété de monolithes de microhoneycomb (MHMs) où le liquide peut passer à travers avec une chute de pression extrêmement faible. MHMs obtenus sont censés être utilisés comme filtres, supports de catalyseur, électrodes de débit-type, des capteurs et des échafaudages pour les biomatériaux.