新しいキャスト MnCuNiFeZnAl 合金の優れた能力と高いサービス温度の減衰の準備のための利用可能な手法
JoVE Journal
Engineering
Author Produced
A subscription to JoVE is required to view this content.  Sign in or start your free trial.
JoVE Journal Engineering
An Available Technique for Preparation of New Cast MnCuNiFeZnAl Alloy with Superior Damping Capacity and High Service Temperature
Please note that all translations are automatically generated. Click here for the English version.

新しいキャスト MnCuNiFeZnAl 合金の優れた能力と高いサービス温度の減衰の準備のための利用可能な手法

DOI:
10.3791/57180-v

•

14:51 min

•

September 23, 2018

•

, , , , ,
1School of Manufacturing Science and Engineering,Sichuan University, 2Department of Mechanical Engineering,Hong Kong Polytechnic University, 3Department of Mechanical and Electrical Engineering,Chengdu Aeronautic Polytechnic

Chapters

  • 00:00Title
  • 01:31Introduction
  • 05:01The Protocol for Alloy Preparation and Test
  • 10:32Representative Results
  • 13:47Conclusion

Summary

Automatic Translation

Automatic Translation

ここで小説の質の高い製錬技術と合理的な熱処理法による優れた包括的なパフォーマンスに Mn-Cu 系合金を取得するためのプロトコルを提案する.

Tags

Cast MnCuNiFeZnAl AlloyDamping CapacityHigh Service TemperatureVacuum Induction MeltingSand Mold CastingHeat TreatmentMicrostructureManganese-copper Based AlloysFace-centered Cubic To Face-centered Tetragonal Phase TransformationAging TreatmentNanoscale Precipitates

Article

Embed

ADD TO PLAYLIST

Usage Statistics

Related Videos

エクストリーム圧力と温度での合成とMicrodiffraction

高分解能温度フィールドマッピングのための光ファイバの分散センサ

高温プラズマ診断として使用するためのX線イメージングクリスタル分光法を適用します

ゼオライトH-ZSM-5で高温・高圧のガス吸着用のLangatateクリスタルマイクロバランスに基づいて吸着装置

イオン液体系電解質、リチウムイオン電池の組立、および高温でのパフォーマンスの測定の合成

キャストアルミ部品の暖かいスピニングのための実験手順

によってナノ構造イットリア安定化ジルコニア（YSZ）足場の高温製作<em>その場での</em>カーボンテンプレート化キセロゲル

ステンレス鋼の滑りやすい表面の作製と高温の反付着挙動

実験室雷アークの広帯域高解像度発光スペクトルの記録方法

磁石は、複合材生産を支援: 柔軟な新しい技術高圧真空袋/Lay アップ プロセスを達成するため

Read Article