Surface Properties of Synthesized Nanoporous Carbon and Silica Matrices

Please note that all translations are automatically generated. Click here for the English version.

합성된 성공 탄소 그리고 실리 카 매트릭스의 표면 특성

DOI:

10.3791/58395-v

•

09:31 min

•

March 27, 2019

•

Angelina Sterczyńska, Małgorzata Śliwińska-Bartkowiak², Małgorzata Zienkiewicz-Strzałka, Anna Deryło-Marczewska

¹Faculty of Physics,Adam Mickiewicz University, ²NanoBioMedical Centre, ³Department of Physicochemistry of Solid Surface, Faculty of Chemistry,Maria Curie-Skłodowska University

Chapters

00:04Title
01:42Synthesis of a Silica Matrix as the Ordered Mesoporous Carbon Material Precursor
03:11Impregnation of the Silica Matrix, using a Carbon Precursor
04:15Tempering and Carbonization
04:46Removal of the Silica Matrix by Etching
06:17Capillary Rise Method for Wettability Measurements
07:23Results: Contact Angles vs. the Microscopic Wetting Parameter Measured Inside the Porous Matrices
08:11Conclusion

Summary

Automatic Translation

여기 우리 합성 및 주문된 성공 (4.6 nm 기 공 크기)와 탄소와 SBA-15 (5.3 nm 기 공 크기)의 특성을 보고합니다. 작업 표면 및 성공 분자 체의 텍스처 속성, 그들의 습윤 D₂O 자료에 국한의 녹는 동작에 설명 합니다.

Article

Embed

ADD TO PLAYLIST

Usage Statistics

Related Videos

전자 레인지를 이용한 산 - 촉매 반응을 통해 실리카 나노 입자의 제조

전자 상자성 공명 및 교정 가스 흐름에 의해 탄소 표면의 급진적 자연 탐험

합성과 메조 포러스 실리카의 벽에 금 층상의 촉매 성능

토양 칼럼을 통해 표면 개질 된 카본 나노 튜브의 운송

실내 온도에서 탄소 나노 시트의 제조

보장<em> N</em> - 헤테로 사이 클릭 카벤 착물 : 벤즈 이미 다 졸리움 염으로부터의 합성 및 탄소 - 탄소 결합 형성 반응에서의 촉매 활성

산화 티타늄<sub> 2</sub소프트 - 화학 방법에 의해 합성 초 소수성 및 높은 IR 반사 특성과> 코팅 된 투명 유리 마이크로 스피어

시간 해결 Photophysical 특성화 Triplet 수확 유기 화합물은 산소가 없는 환경을 사용 하 여는 iCCD 카메라

라만 방법과 IR Spectroelectrochemical 도구로 활용 된 유기 화합물을 분석 하

Bioinspired 메서드를 사용 하 여 기능성 실리 카의 준비

Read Article